NORYL™ Resin N850 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ N850 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high flow, injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VA at 3mm and V0 at 1.5mm along with UL746C Outdoor Suitability rating of F2. NORYL N850 resin exhibits high impact strength, dimensional stability, hydrolytic stability, and very low moisture absorption. This material is an excellent candidate for electrical and business equipment applications.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Limiting oxygen index	23.0 °C	36.4 % Show Supplier Material materials with Limiting oxygen index of 36.4 %
Relative density	23.0 °C	1.13 [-] Show Supplier Material materials with Relative density of 1.13 [-]	ASTM D 792 \|

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	3 GPa Show Supplier Material materials with Elastic modulus of 3 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	3.2 % Show Supplier Material materials with Elongation of 3.2 %	ISO 527 \| yield, 50 mm/min
Flexural modulus	23.0 °C	2.6 GPa Show Supplier Material materials with Flexural modulus of 2.6 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	107 MPa Show Supplier Material materials with Flexural strength of 107 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Izod notched	23.0 °C	10 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 10 kJ/m²	ISO 180/1A \| notched 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	213 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 213 J/m	ASTM D 256 \| notched, 23°C
Instrumented Impact, Total Energy	23.0 °C	31 J Show Supplier Material materials with Instrumented Impact, Total Energy of 31 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	61 MPa Show Supplier Material materials with Tensile strength of 61 MPa	ISO 527 \| break, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	7.74E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.74E-5 1/K	ASTM E 831 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	8.1E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.1E-5 1/K	ASTM E 831 \| -40°C to 40°C
Heat deflection temperature		82 - 95 °C Show Supplier Material materials with Heat deflection temperature of 82 - 95 °C
Heat deflection temperature, 0.45 MPa		95 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 95 °C	ISO 75/Bf \| Flatw 80104 sp=64mm
Heat deflection temperature, 1.80 MPa		82 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 82 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Relative temperature index, electrical		50 °C Show Supplier Material materials with Relative temperature index, electrical of 50 °C	UL 746B
Relative temperature index, mechanical impact		50 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 50 °C	UL 746B
Relative temperature index, mechanical strength		50 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 50 °C	UL 746B
Vicat softening temperature		108 °C Show Supplier Material materials with Vicat softening temperature of 108 °C	ISO 306 \| Rate B/120
Flammability	UL Recognized, 94HB Flame Class Rating: 0.99mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: 1.49mm UL 94 <br> UL Recognized, 94-5VA Flame Class Rating: 2.99mm UL 94 <br> UV-light, water exposure/immersion: F2- UL 746C

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	2 V Show Supplier Material materials with Comparative tracking index of 2 V	UL 746A \| (UL) {PLC}
High Amp Arc Ignition	23.0 °C	2 mm Show Supplier Material materials with High Amp Arc Ignition of 2 mm	UL 746A \| surface {PLC}
High Volt Arc Track Rate	23.0 °C	4 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code	UL 746A \| (PLC)
Hot-Wire Ignition	23.0 °C	2 mm Show Supplier Material materials with Hot-Wire Ignition of 2 mm	UL 746A \| (PLC)

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		14 g/10min Show Supplier Material materials with Melt mass-flow rate of 14 g/10min	ASTM D 1238 \| 220°C/2.16 kgf
Shrinkage	23.0 °C	0.5 % Show Supplier Material materials with Shrinkage of 0.5 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Document Handling
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 75 to 80.0°C Drying Time: 3 to 4.0hrs Drying Time (Cumulative): 8hrs Maximum Moisture Content: -0.02% Melt Temperature: 250 to 275.0°C Nozzle Temperature: 250 to 275.0°C Front - Zone 3 Temperature: 240 to 275.0°C Middle - Zone 2 Temperature: 225 to 270.0°C Rear - Zone 1 Temperature: 215 to 265.0°C Mold Temperature: 55 to 75.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 20 to 100.0rpm Shot to Cylinder Size: 30 to 70.0% Vent Depth: 0.038 to 0.051mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.