LNP™ COLORCOMP™ D1000RF is an unfilled compound based on Polycarbonate resin. Added features of this grade include: Non-Halogenated, Mold Release, UL Rated HB. Good for small, intricate parts.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.19 g/cm³

Show Supplier Material materials with Density of 1.19 g/cm³

ASTM D 792

Relative density

23.0 °C

1.2 [-]

Show Supplier Material materials with Relative density of 1.2 [-]

ASTM D 792

Specific volume

23.0 °C

0.83 cm³/g

Show Supplier Material materials with Specific volume of 0.83 cm³/g

ASTM D 792

Water absorption

23.0 °C

0.58 %

Show Supplier Material materials with Water absorption of 0.58 %

ASTM D 570 | equilibrium, 100°C

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

7 %

Show Supplier Material materials with Elongation of 7 %

ASTM D 638 | yld, Type I, 50 mm/min

Flexural modulus

23.0 °C

2.34 GPa

Show Supplier Material materials with Flexural modulus of 2.34 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

96 MPa

Show Supplier Material materials with Flexural strength of 96 MPa

ASTM D 790 | yld, 1.3 mm/min, 50 mm span

Hardness, Rockwell M

23.0 °C

70 [-]

Show Supplier Material materials with Hardness, Rockwell M of 70 [-]

ASTM D 785 |

Hardness, Rockwell R

23.0 °C

118 [-]

Show Supplier Material materials with Hardness, Rockwell R of 118 [-]

ASTM D 785

Impact strength, Charpy notched

23.0 °C

65 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 65 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

65 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 65 kJ/m²

ISO 180/1A | 80*10*3, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

694 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 694 J/m

ASTM D 256 | notched, 23°C

Impact strength, Izod unnotched, ASTM

23.0 °C

3204 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 3204 J/m

ASTM D 4812 | 23°C

Instrumented Impact, at Peak

23.0 °C

62 J

Show Supplier Material materials with Instrumented Impact, at Peak of 62 J

ASTM D 3763 | 23°C

Taber Abrasion

23.0 °C

10 mg/1000cy

Show Supplier Material materials with Taber Abrasion of 10 mg/1000cy

ASTM D 1044 | CS-17, 1 kg

Tensile strength

23.0 °C

68 MPa

Show Supplier Material materials with Tensile strength of 68 MPa

ASTM D 638 | brk, Type I, 50 mm/min

Impact strength, Charpy unnotched

ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C

Impact strength, Izod unnotched

ISO 180/1U | 80*10*3, 23°C

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

6.84E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 6.84E-5 1/K

ASTM E 831 | -40°C to 95°C

Heat deflection temperature, 0.45 MPa

137 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 137 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

129 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 129 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

130 °C

Show Supplier Material materials with Relative temperature index, electrical of 130 °C

UL 746B

Relative temperature index, mechanical impact

130 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 130 °C

UL 746B

Relative temperature index, mechanical strength

130 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 130 °C

UL 746B

Specific heat capacity

23.0 °C

1.25E-3 J/(kg·K)

Show Supplier Material materials with Specific heat capacity of 1.25E-3 J/(kg·K)

ASTM C 351

Thermal conductivity

23.0 °C

0.25 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.25 W/(m·K)

ASTM C177

Vicat softening temperature

154 °C

Show Supplier Material materials with Vicat softening temperature of 154 °C

ASTM D 1525 | Rate B/50

Flammability

UL Yellow Card Link: br UL Recognized, 94HB Flame Class Rating: 0.7 mm UL 94 br Radiant Panel Listing: TRUE

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

2 V

Show Supplier Material materials with Comparative tracking index of 2 V

UL 746A | (UL) {PLC}

Dielectric constant, 1MHz

23.0 °C

2.96 [-]

Show Supplier Material materials with Dielectric constant, 1MHz of 2.96 [-]

ASTM D 150

Dielectric constant, 60Hz

23.0 °C

3.17 [-]

Show Supplier Material materials with Dielectric constant, 60Hz of 3.17 [-]

ASTM D 150 | 50/60 Hz

Dielectric strength

23.0 °C

14.9 kV/mm

Show Supplier Material materials with Dielectric strength of 14.9 kV/mm

ASTM D 149 | in air, 3.2 mm

Dissipation factor, 1MHz

23.0 °C

0.01 [-]

Show Supplier Material materials with Dissipation factor, 1MHz of 0.01 [-]

ASTM D 150

Dissipation factor, 50Hz

23.0 °C

9E-4 [-]

Show Supplier Material materials with Dissipation factor, 50Hz of 9E-4 [-]

ASTM D 150 | 50/60 Hz

High Amp Arc Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm

UL 746A | PLC 0

High Volt Arc Track Rate

23.0 °C

4 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

1.1 mm

Show Supplier Material materials with Hot-Wire Ignition of 1.1 mm

UL 746A | PLC 3

Volume resistivity

23.0 °C

1.00E+17 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm

ASTM D 257

Optical

PropertyValueComment

Haze

1 %

Show Supplier Material materials with Haze of 1 %

ASTM D 1003 | 2.54 mm

Refractive index

1.59 [-]

Show Supplier Material materials with Refractive index of 1.59 [-]

ASTM D542

Transmission

88 %

Show Supplier Material materials with Transmission of 88 %

ASTM D 1003 | 2.54 mm

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

17.5 g/10min

Show Supplier Material materials with Melt mass-flow rate of 17.5 g/10min

ASTM D 1238 | 300°C/1.2 kgf

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Electronic Components

Availability

Europe,Asia,Americas

Features

Custom Color, Appearance & Durability

Processing methods

Drying Temperature: 120 °C br Drying Time: 3 to 4.0 hrs br Drying Time (Cumulative): 48 hrs br Maximum Moisture Content: 0.02 % br Melt Temperature: 280 to 305.0 °C br Nozzle Temperature: 275 to 300.0 °C br Front

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.