General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.19 g/cm³ Show Supplier Material materials with Density of 1.19 g/cm³ | ISO 1183 |
Relative density | 23.0 °C | 1.2 [-] Show Supplier Material materials with Relative density of 1.2 [-] | ASTM D 792 | |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 2.1 % Show Supplier Material materials with Elongation of 2.1 % | ISO 527 | yield, 50 mm/min |
Flexural modulus | 23.0 °C | 2.7 GPa Show Supplier Material materials with Flexural modulus of 2.7 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural strength | 23.0 °C | 71 MPa Show Supplier Material materials with Flexural strength of 71 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Impact strength, Charpy notched | 23.0 °C | 19 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 19 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Impact strength, Izod notched | 23.0 °C | 18 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 18 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 213 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 213 J/m | ASTM D 256 | notched, 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 33 J Show Supplier Material materials with Instrumented Impact, Total Energy of 33 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 41 MPa Show Supplier Material materials with Tensile strength of 41 MPa | ISO 527 | yield, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.46E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 8.46E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8.64E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.64E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature | 73 - 82 °C Show Supplier Material materials with Heat deflection temperature of 73 - 82 °C | ||||
Heat deflection temperature, 0.45 MPa | 82 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 82 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 73 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 73 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 60 °C Show Supplier Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |||
Relative temperature index, mechanical impact | 60 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |||
Relative temperature index, mechanical strength | 60 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |||
Vicat softening temperature | 81 °C Show Supplier Material materials with Vicat softening temperature of 81 °C | ISO 306 | Rate B/50 | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103956750- - <br> UL Recognized, 94-5VA Flame Class Rating: ≥2.5mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UV-light, water exposure/immersion: F2- UL 746C |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 2 V Show Supplier Material materials with Comparative tracking index of 2 V | UL 746A | (UL) {PLC} |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 4 |
High Volt Arc Track Rate | 23.0 °C | 4 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 3 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 10 g/10min Show Supplier Material materials with Melt mass-flow rate of 10 g/10min | ISO 1133 | 220°C/5.0 kg | |
Melt viscosity | 23.0 °C | 290 Pa·s Show Supplier Material materials with Melt viscosity of 290 Pa·s | ASTM D 3825 | 200°C, 1000 sec-1 |
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80 to 90.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |