LNP™ LUBRILOY™ Compound ZX06315

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRILOY ZX06315 is a compound based on PPE+PS Blend resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Internally Lubricated, Non-Brominated & Non-Chlorinated Flame Retardant, Flame Retardant, high HDT.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Coefficient of friction		0.21 [-] Show Supplier Material materials with Coefficient of friction of 0.21 [-]
Coefficient of friction, kinetic		0.21 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.21 [-]	ASTM D 3702 Modified: Manual
Density	23.0 °C	1.07 g/cm³ Show Supplier Material materials with Density of 1.07 g/cm³	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa	ASTM D 638 \| 50 mm/min
Elongation	23.0 °C	11.9 % Show Supplier Material materials with Elongation of 11.9 %	ASTM D 638 \| brk, Type I, 50 mm/min
Flexural modulus	23.0 °C	2.2 GPa Show Supplier Material materials with Flexural modulus of 2.2 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	91 MPa Show Supplier Material materials with Flexural strength of 91 MPa	ASTM D 790 \| brk, 1.3 mm/min, 50 mm span
Hardness, Rockwell R	23.0 °C	115 [-] Show Supplier Material materials with Hardness, Rockwell R of 115 [-]	ASTM D 785
Impact strength, Izod notched	23.0 °C	230 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 230 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	230 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 230 J/m	ASTM D 256 \| notched, 23°C
Tensile strength	23.0 °C	50 MPa Show Supplier Material materials with Tensile strength of 50 MPa	ASTM D 638 \| brk, Type I, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	7.2E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.2E-4 1/K	ASTM E 831 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	8.6E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.6E-4 1/K	ASTM E 831 \| -40°C to 40°C
Heat deflection temperature		124 °C Show Supplier Material materials with Heat deflection temperature of 124 °C
Heat deflection temperature, 1.80 MPa		124 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 124 °C	ASTM D 648 \| 3.2mm, unannealed
Relative temperature index, electrical		65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C	UL 746B
Relative temperature index, mechanical impact		65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C	UL 746B
Relative temperature index, mechanical strength		65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C	UL 746B
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101284063- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=102991929- - <br> UL Recognized, 94V-1 Flame Class Rating: ≥1.5mm UL 94

Rheological Properties

Property	Temperature	Value	Comment
Melt volume-flow rate		38 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 38 cm³/10min	ISO 1133 \| MVR at 280°C/10.0 kg
Shrinkage	23.0 °C	0.94 % Show Supplier Material materials with Shrinkage of 0.94 %	ASTM D 955 \| 24 hrs
Shrinkage, transverse	23.0 °C	0.91 % Show Supplier Material materials with Shrinkage, transverse of 0.91 %	ASTM D 955 \| 24 hrs

Technological properties

Property
Application areas	Document Handling
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 80°C Drying Time: 3 to 4.0hrs Melt Temperature: 270 to 295.0°C Nozzle Temperature: 265 to 275.0°C Front - Zone 3 Temperature: 265 to 275.0°C Middle - Zone 2 Temperature: 260 to 270.0°C Rear - Zone 1 Temperature: 255 to 265.0°C Mold Temperature: 60 to 95.0°C Back Pressure: 0.2 to 0.4MPa Screw Speed: 40 to 100.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.