LNP™ COLORCOMP™ Compound 61000EUI

Want to keep this datasheet? Save it now in your required format

Description

LNP* COLORCOMP* 61000EUI is an unreinforced compound based on PBT+PC Alloy. Added features of this grade include: Impact Modified, improved retention of mechanical properties under UV exposure and excellent low temperature impact and chemical resistance.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperatureComment

Density

1.22 g/cm³

Show Supplier Material materials with Density of 1.22 g/cm³ at 23.0 °C

23.0 °C

ISO 1183

Moisture absorption

0.15 %

Show Supplier Material materials with Moisture absorption of 0.15 % at 23.0 °C

23.0 °C

ISO 62 | (23°C / 50% RH)

Relative density

1.21 [-]

Show Supplier Material materials with Relative density of 1.21 [-] at 23.0 °C

23.0 °C

ASTM D 792

Specific volume

0.83 cm³/g

Show Supplier Material materials with Specific volume of 0.83 cm³/g at 23.0 °C

23.0 °C

ASTM D 792

Water absorption

0.5 %

Show Supplier Material materials with Water absorption of 0.5 % at 23.0 °C

23.0 °C

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyValueTemperatureComment

Elastic modulus

2.05 GPa

Show Supplier Material materials with Elastic modulus of 2.05 GPa at 23.0 °C

23.0 °C

ISO 527 | 1 mm/min

Elongation

120 %

Show Supplier Material materials with Elongation of 120 % at 23.0 °C

23.0 °C

ISO 527 | break, 50 mm/min

Flexural modulus

2 GPa

Show Supplier Material materials with Flexural modulus of 2 GPa at 23.0 °C

23.0 °C

ISO 178 | 2 mm/min

Flexural strength

80 MPa

Show Supplier Material materials with Flexural strength of 80 MPa at 23.0 °C

23.0 °C

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

55 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 55 kJ/m² at 23.0 °C

23.0 °C

ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C

Impact strength, Izod notched

30 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 30 kJ/m² at 23.0 °C

23.0 °C

ISO 180/1A | notched 80*10*4, -30°C

Impact strength, Izod notched, ASTM

530 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 530 J/m at 23.0 °C

23.0 °C

ASTM D 256 | notched, -30°C

Instrumented Impact, Total Energy

60 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 60 J at 23.0 °C

23.0 °C

ASTM D 3763 | 23°C

Tensile strength

50 MPa

Show Supplier Material materials with Tensile strength of 50 MPa at 23.0 °C

23.0 °C

ISO 527 | yield, 50 mm/min

Thermal

PropertyValueTemperatureComment

Coefficient of thermal expansion

9.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 9.5E-5 1/K at 23.0 °C

23.0 °C

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

9.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 9.5E-5 1/K at 23.0 °C

23.0 °C

ISO 11359-2 | -40°C to 40°C

Flammability

UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103952713 | UL Recognized, 94HB Flame Class Rating: 1.5 mm UL 94 | UV-light, water exposure/immersion: F2 - UL 746C | UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=103938363

Heat deflection temperature, 0.45 MPa

107 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 107 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

75 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 75 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Relative temperature index, electrical

75 °C

Show Supplier Material materials with Relative temperature index, electrical of 75 °C

UL 746B

Relative temperature index, mechanical impact

75 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 75 °C

UL 746B

Relative temperature index, mechanical strength

75 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 75 °C

UL 746B

Vicat softening temperature

120 °C

Show Supplier Material materials with Vicat softening temperature of 120 °C

ISO 306 | Rate B/50

Electrical

PropertyValueTemperatureComment

Comparative tracking index

1 V

Show Supplier Material materials with Comparative tracking index of 1 V at 23.0 °C

23.0 °C

UL 746A | (UL) {PLC}

High Amp Arc Ignition

1.5 mm

Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm at 23.0 °C

23.0 °C

UL 746A | PLC 0

High Volt Arc Track Rate

0 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 0 PLC Code at 23.0 °C

23.0 °C

UL 746A | (PLC)

Hot-Wire Ignition

1.5 mm

Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm at 23.0 °C

23.0 °C

UL 746A | PLC 3

Rheological Properties

PropertyValueTemperatureComment

Melt mass-flow rate

16 g/10min

Show Supplier Material materials with Melt mass-flow rate of 16 g/10min

ISO 1133 | 250°C/5.0 kg

Melt volume-flow rate

15 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 15 cm³/10min

ISO 1133 | MVR at 250°C/5.0 kg

Shrinkage

0.8 %

Show Supplier Material materials with Shrinkage of 0.8 % at 23.0 °C

23.0 °C

SABIC method | 3.2 mm

Shrinkage, transverse

0.8 %

Show Supplier Material materials with Shrinkage, transverse of 0.8 % at 23.0 °C

23.0 °C

SABIC method | on tensile bar

Technological properties

Property
Application areas

Electronic Components, Individual Equiptment

Availability

Europe,Asia,Americas

Processing methods

Drying Temperature: 110 °C | Drying Time: 4 to 6.0 hrs | Drying Time (Cumulative): 8 hrs | Maximum Moisture Content: 0.02 % | Melt Temperature: 260 to 275.0 °C | Nozzle Temperature: 255 to 270.0 °C | Front - Zone 3 Temperature: 255 to 275.0 °C | Middle - Zone 2 Temperature: 250 to 270.0 °C | Rear - Zone 1 Temperature: 245 to 265.0 °C | Mold Temperature: 65 to 90.0 °C | Back Pressure: 0.3 to 0.7 MPa | Screw Speed: 50 to 80.0 rpm | Shot to Cylinder Size: 50 to 80.0 % | Vent Depth: 0.013 to 0.02 mm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.