General
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 4 - 6 % Show Supplier Material materials with Elongation of 4 - 6 % | SABIC - Japan Method | break |
Flexural modulus | 23.0 °C | 10.3 GPa Show Supplier Material materials with Flexural modulus of 10.3 GPa | ASTM D 790 |
Flexural strength | 23.0 °C | 154 MPa Show Supplier Material materials with Flexural strength of 154 MPa | ASTM D 790 |
Hardness, Rockwell M | 23.0 °C | 90 [-] Show Supplier Material materials with Hardness, Rockwell M of 90 [-] | ASTM D 785 | |
Impact strength, Izod notched | 23.0 °C | 68 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 68 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 68 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 68 J/m | ASTM D 256 | notched, 23°C |
Tensile strength | 23.0 °C | 116 MPa Show Supplier Material materials with Tensile strength of 116 MPa | SABIC - Japan Method | yield |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.1E-5 - 3.3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.1E-5 - 3.3E-5 1/K | TMA | -30°C to 30°C | ||
Heat deflection temperature | 125 °C Show Supplier Material materials with Heat deflection temperature of 125 °C | ||||
Heat deflection temperature, 1.80 MPa | 125 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 125 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=228551- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 1.00E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+16 Ω | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 15.4 g/10min Show Supplier Material materials with Melt mass-flow rate of 15.4 g/10min | ASTM D 1238 | 300°C/2.16 kgf | |
Shrinkage | 23.0 °C | 0.15 % Show Supplier Material materials with Shrinkage of 0.15 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing, Small Appliance, Power Manangement, Wireless Communications, Building Accessory, Document Handling, Displays, Electronic Components, Enclosures | |
Availability | Europe,Asia,MEA,Americas | |
Processing methods | Back Pressure: 0.3 to 0.7MPa | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |