LNP™ STAT-KON™ Compound JK800

Want to keep this datasheet? Save it now in your required format

Description

LNP™ STAT-KON™ JK800 compound is a 8% carbon fiber reinforced PC+ABS, electrostatic dissipative ECO conforming FR. Good hydrolytic stability.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Consumer Goods

Domestic Electrical Appliances

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.25 [-] Show Supplier Material materials with Relative density of 1.25 [-]	ASTM D 792 \|

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	7.5 GPa Show Supplier Material materials with Elastic modulus of 7.5 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	1.9 % Show Supplier Material materials with Elongation of 1.9 %	ISO 527 \| yield, 5 mm/min
Flexural modulus	23.0 °C	6.4 GPa Show Supplier Material materials with Flexural modulus of 6.4 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	145 MPa Show Supplier Material materials with Flexural strength of 145 MPa	ISO 178 \| break, 2 mm/min
Impact strength, Izod notched	23.0 °C	4 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 4 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	37 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 37 J/m	ASTM D 256 \| notched, 23°C
Impact strength, Izod unnotched	23.0 °C	21 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 21 kJ/m²	ISO 180/1U \| 80104, 23°C
Impact strength, Izod unnotched, ASTM	23.0 °C	347 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 347 J/m	ASTM D 4812 \| 23°C
Instrumented Impact, Total Energy	23.0 °C	82 J Show Supplier Material materials with Instrumented Impact, Total Energy of 82 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	95 MPa Show Supplier Material materials with Tensile strength of 95 MPa	ISO 527 \| yield, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	2.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.6E-5 1/K	ISO 11359-2 \| 23°C to 80°C
Coefficient of thermal expansion, transverse	23.0 °C	7.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.4E-5 1/K	ISO 11359-2 \| 23°C to 80°C
Heat deflection temperature		92 - 97 °C Show Supplier Material materials with Heat deflection temperature of 92 - 97 °C
Heat deflection temperature, 0.45 MPa		97 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 97 °C	ASTM D 648 \| 3.2 mm, unannealed
Heat deflection temperature, 1.80 MPa		92 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 92 °C	ASTM D 648 \| 3.2mm, unannealed
Relative temperature index, electrical		60 °C Show Supplier Material materials with Relative temperature index, electrical of 60 °C	UL 746B
Relative temperature index, mechanical impact		60 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 60 °C	UL 746B
Relative temperature index, mechanical strength		60 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 60 °C	UL 746B
Vicat softening temperature		101 °C Show Supplier Material materials with Vicat softening temperature of 101 °C	ISO 306 \| Rate B/120
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221061- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=101632098- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥1mm UL 94 <br> UL Recognized, 94-5VB Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Ignitability Temperature, 1.5 mm: 800°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12

Electrical

Property	Temperature	Value	Comment
High Amp Arc Ignition	23.0 °C	1 mm Show Supplier Material materials with High Amp Arc Ignition of 1 mm	≥, UL 746A \| PLC 0
Hot-Wire Ignition	23.0 °C	1 mm Show Supplier Material materials with Hot-Wire Ignition of 1 mm	≥, UL 746A \| PLC 0
Sheet resistivity, ROA	23.0 °C	1000000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1000000 Ω	ASTM D 257
Volume resistivity	23.0 °C	1000 Ω·cm Show Supplier Material materials with Volume resistivity of 1000 Ω·cm	ASTM D 257

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		17 g/10min Show Supplier Material materials with Melt mass-flow rate of 17 g/10min	ASTM D 1238 \| 260°C/2.16 kgf
Shrinkage	23.0 °C	0.1 % Show Supplier Material materials with Shrinkage of 0.1 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	0.2 % Show Supplier Material materials with Shrinkage, transverse of 0.2 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Electronic Components, Wiring Devices, Vacuum Cleaner
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 75 to 80.0°C Drying Time: 3 to 4.0hrs Drying Time (Cumulative): 8hrs Maximum Moisture Content: 0.04% Melt Temperature: 230 to 275.0°C Nozzle Temperature: 230 to 275.0°C Front - Zone 3 Temperature: 225 to 275.0°C Middle - Zone 2 Temperature: 215 to 260.0°C Rear - Zone 1 Temperature: 210 to 255.0°C Mold Temperature: 50 to 70.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 40 to 70.0rpm Shot to Cylinder Size: 30 to 80.0% Vent Depth: 0.038 to 0.076mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.