Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.7 GPa Show Supplier Material materials with Elastic modulus of 2.7 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 6.5 % Show Supplier Material materials with Elongation of 6.5 % | ASTM D 638 | yld, Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 2.6 GPa Show Supplier Material materials with Flexural modulus of 2.6 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural strength | 23.0 °C | 125 MPa Show Supplier Material materials with Flexural strength of 125 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Impact strength, Izod notched | 23.0 °C | 53 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 53 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 53 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 53 J/m | ASTM D 256 | notched, 23°C |
Tensile strength | 23.0 °C | 88 MPa Show Supplier Material materials with Tensile strength of 88 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.2E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5.2E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Heat deflection temperature | 200 °C Show Supplier Material materials with Heat deflection temperature of 200 °C | ||||
Heat deflection temperature, 1.80 MPa | 200 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 200 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 180 °C Show Supplier Material materials with Relative temperature index, electrical of 180 °C | UL 746B | |||
Relative temperature index, mechanical impact | 170 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C | UL 746B | |||
Relative temperature index, mechanical strength | 180 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 180 °C | UL 746B | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101283890- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.81mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.43mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.43mm UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dissipation factor, 1MHz | 23.0 °C | 5.6E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 5.6E-3 [-] | ASTM D 150 | |
Dissipation factor, 1kHz | 23.0 °C | 2.2E-3 [-] Show Supplier Material materials with Dissipation factor, 1kHz of 2.2E-3 [-] | ASTM D 150 |
Dissipation factor, 50Hz | 23.0 °C | 1.7E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 1.7E-3 [-] | ASTM D 150 | 50/60 Hz |
High Amp Arc Ignition | 23.0 °C | 0.43 mm Show Supplier Material materials with High Amp Arc Ignition of 0.43 mm | ≥, UL 746A | PLC 0 |
Hot-Wire Ignition | 23.0 °C | 0.81 mm Show Supplier Material materials with Hot-Wire Ignition of 0.81 mm | ≥, UL 746A | PLC 3 |
Volume resistivity | 23.0 °C | 1.75E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.75E+15 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.6 % Show Supplier Material materials with Shrinkage of 0.6 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120 to 150.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |