General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.37 g/cm³ Show Supplier Material materials with Density of 1.37 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.9 % Show Supplier Material materials with Water absorption of 0.9 % | ISO 62-1 | (23°C/24hrs) |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.7 GPa Show Supplier Material materials with Elastic modulus of 2.7 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 6.8 % Show Supplier Material materials with Elongation of 6.8 % | ISO 527 | yield, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.8 GPa Show Supplier Material materials with Flexural modulus of 2.8 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 136 MPa Show Supplier Material materials with Flexural strength of 136 MPa | ISO 178 | yield, 2 mm/min | ||
Impact strength, Izod notched | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 7 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C | ||
Tensile strength | 23.0 °C | 65 MPa Show Supplier Material materials with Tensile strength of 65 MPa | ISO 527 | break, 50 mm/min | ||
Impact strength, Izod unnotched | ISO 180/1U | unnotched 80*10*4 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5.6E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 5.7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.7E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature | 197 °C Show Supplier Material materials with Heat deflection temperature of 197 °C | ||||
Heat deflection temperature, 1.80 MPa | 197 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 197 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 180 °C Show Supplier Material materials with Relative temperature index, electrical of 180 °C | UL 746B | |||
Relative temperature index, mechanical impact | 170 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C | UL 746B | |||
Relative temperature index, mechanical strength | 180 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 180 °C | UL 746B | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101283858- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.81mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.43mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.43mm UL 94 |
Electrical
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.9 % Show Supplier Material materials with Shrinkage of 0.9 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120 to 150.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |