LNP™ COLORCOMP™ Compound AX98567H

Want to keep this datasheet? Save it now in your required format

Description

LNP* COLORCOMP* AX98567H is an unfilled compound based on ABS. Added feature of this grade is: Healthcare.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Healthcare

Medical Equipment

Surgical Instruments

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.06 [-] Show Supplier Material materials with Relative density of 1.06 [-]	ASTM D 792 \|

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.5 GPa Show Supplier Material materials with Elastic modulus of 2.5 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	2 % Show Supplier Material materials with Elongation of 2 %	ISO 527 \| yield, 5 mm/min
Flexural modulus	23.0 °C	2.6 GPa Show Supplier Material materials with Flexural modulus of 2.6 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	75 MPa Show Supplier Material materials with Flexural strength of 75 MPa	ISO 178
Impact strength, Charpy notched	23.0 °C	11 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²	ISO 179/2C \| 23°C
Impact strength, Charpy unnotched	23.0 °C	70 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 70 kJ/m²	ISO 179/2C \| -30°C
Impact strength, Izod notched	23.0 °C	12 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m²	ISO 180/1A \| 80104, 23°C
Tensile strength	23.0 °C	52 MPa Show Supplier Material materials with Tensile strength of 52 MPa	ISO 527 \| yield, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 8E-5 1/K	ISO 11359-2 \| 23°C to 60°C
Relative temperature index, electrical		80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C	UL 746B
Relative temperature index, mechanical impact		80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C	UL 746B
Relative temperature index, mechanical strength		80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C	UL 746B
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101343432- - <br> UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94

Electrical

Property	Temperature	Value	Comment
High Amp Arc Ignition	23.0 °C	1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm	≥, UL 746A \| PLC 0
High Volt Arc Track Rate	23.0 °C	1 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 1 PLC Code	UL 746A \| (PLC)
Hot-Wire Ignition	23.0 °C	1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm	≥, UL 746A \| PLC 4
Sheet resistivity, ROA	23.0 °C	1.00E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+16 Ω	IEC 60093
Volume resistivity	23.0 °C	1.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 Ω·cm	IEC 60093

Rheological Properties

Property	Temperature	Value	Comment
Melt volume-flow rate		27 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 27 cm³/10min	ISO 1133 \| MVR at 230°C/10.0 kg
Shrinkage	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage of 0.4 %	ISO 294 \| 24 hrs
Shrinkage, transverse	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage, transverse of 0.4 %	ISO 294 \| 24 hrs

Technological properties

Property
Application areas	Surgical Devices, Medical Device
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 80°C Drying Time: 4hrs Maximum Moisture Content: 0.05 to 0.1% Melt Temperature: 260°C Front - Zone 3 Temperature: 265 to 275.0°C Middle - Zone 2 Temperature: 230 to 245.0°C Rear - Zone 1 Temperature: 205 to 215.0°C Mold Temperature: 70 to 80.0°C Back Pressure: 0.2 to 0.3MPa Screw Speed: 30 to 60.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.