ULTEM™ Resin 1000 - Americas

Want to keep this datasheet? Save it now in your required format

Description

ULTEM 1000 resin is an amorphous, transparent polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217°C. This inherently flame retardant resin has UL94 V0, V2 and 5VA ratings and is RoHS compliant. ULTEM 1000 resin is an unreinforced general purpose grade offering high heat resistance, high strength and modulus and broad chemical resistance up to high temperatures.

Ashby charts

See where ULTEM™ Resin 1000 - Americas falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

1.27 g/cm³ at 23 °C

ISO 1183

Limiting oxygen index

LOI

47 % at 23 °C

Moisture absorption

cmoisture

0.7 % at 23 °C

ISO 62 | (23°C / 50% RH)

Relative density

ρrel

1.27 [-] at 23 °C

ASTM D 792 |

Water absorption

cwater

1.25 % at 23 °C

ASTM D 570 | (23°C/Saturated)

Mechanical

Elastic modulus

E

3.58 GPa at 23 °C

Show Polyetherimide (PEI) materials with Elastic modulus of 3.58 GPa at 23 °C

ASTM D 638 | 5 mm/min

Elongation

A

7 % at 23 °C

Show Polyetherimide (PEI) materials with Elongation of 7 % at 23 °C

ASTM D 638 | yld, Type I, 5 mm/min

Flexural modulus

Ebend

3.51 GPa at 23 °C

Show Polyetherimide (PEI) materials with Flexural modulus of 3.51 GPa at 23 °C

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

σbend

165 MPa at 23 °C

Show Polyetherimide (PEI) materials with Flexural strength of 165 MPa at 23 °C

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Hardness, Ball Indentation

HBI

140 MPa at 23 °C

Show Polyetherimide (PEI) materials with Hardness, Ball Indentation of 140 MPa at 23 °C

ISO 2039-1 | H358/30

Hardness, Rockwell M

HRM

109 [-] at 23 °C

Show Polyetherimide (PEI) materials with Hardness, Rockwell M of 109 [-] at 23 °C

ASTM D 785 |

Impact strength, Charpy notched

Ivnot

10 kJ/m² at 23 °C

Show Polyetherimide (PEI) materials with Impact strength, Charpy notched of 10 kJ/m² at 23 °C

ISO 179/2C | 23°C

Impact strength, Izod notched

IIzod,not

53 kJ/m² at 23 °C

Show Polyetherimide (PEI) materials with Impact strength, Izod notched of 53 kJ/m² at 23 °C

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

IIzod,not,astm

53 J/m at 23 °C

Show Polyetherimide (PEI) materials with Impact strength, Izod notched, ASTM of 53 J/m at 23 °C

ASTM D 256

Impact strength, Izod unnotched IIzod,unnot

ISO 180/1U | 80*10*4, 23°C

Impact strength, Izod unnotched, ASTM

IIzod,unnot,astm

1335 J/m at 23 °C

Show Polyetherimide (PEI) materials with Impact strength, Izod unnotched, ASTM of 1335 J/m at 23 °C

ASTM D 4812 | 23°C

Poisson's ratio

ν

0.36 [-] at 23 °C

Show Polyetherimide (PEI) materials with Poisson's ratio of 0.36 [-] at 23 °C

ASTM E 132

Taber Abrasion

TA

10 mg/1000cy at 23 °C

Show Polyetherimide (PEI) materials with Taber Abrasion of 10 mg/1000cy at 23 °C

ASTM D 1044 | CS-17, 1 kg

Tensile strength

Rm

110 MPa at 23 °C

Show Polyetherimide (PEI) materials with Tensile strength of 110 MPa at 23 °C

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

Ball Pressure Test

nan

Coefficient of thermal expansion

α

5.58E-5 1/K at 23 °C

ASTM E 831 | -20°C to 150°C

Coefficient of thermal expansion, transverse

αtrans

5.4E-5 1/K at 23 °C

ASTM E 831 | -20°C to 150°C

Flammability

NBS Smoke Density, Flaming, Ds 4 min: 0.7 - ASTM E 662 | UL Recognized, 94-5VA Flame Class Rating: 3 mm UL 94 | UL Recognized, 94V-0 Flame Class Rating: 0.75 mm UL 94 | UL Recognized, 94V-2 Flame Class Rating: 0.4 mm UL 94 | UL Recognized, 94V-2 Flame Class Rating: 0.4 mm UL 94 | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101048254 | UV-light, water exposure/immersion: F2 - UL 746C

Heat deflection temperature, 0.45 MPa

HDT0.45,MPa

210 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

HDT1.8,MPa

201 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

RTIel

170 °C

UL 746B

Relative temperature index, mechanical impact

RTIimp

170 °C

UL 746B

Relative temperature index, mechanical strength

RTIstr

170 °C

UL 746B

Thermal conductivity

λ

0.22 W/(m·K) at 23 °C

ASTM C177

Vicat softening temperature

Tsoft

218 °C

ASTM D 1525 | Rate B/50

Electrical

Comparative tracking index

CTI

4 V at 23 °C

UL 746A | (UL) {PLC}

Dielectric constant, 100Hz

εr,100Hz

3.15 [-] at 23 °C

ASTM D 150

Dielectric constant, 1MHz

εr,1MHz

2.9 [-] at 23 °C

IEC 60250

Dielectric constant, 60Hz

εr,60Hz

2.9 [-] at 23 °C

IEC 60250 | 50/60 Hz

Dielectric strength

EDS

19.7 kV/mm at 23 °C

ASTM D 149 | in oil, 3.2 mm

Dissipation factor

ε''

2.5E-3 [-] at 23 °C

ASTM D 150 | 2450 MHz

Dissipation factor, 100Hz

ε''100Hz

1.5E-3 [-] at 23 °C

ASTM D 150

Dissipation factor, 1MHz

ε''1MHz

6E-3 [-] at 23 °C

IEC 60250

Dissipation factor, 1kHz

ε''1KHz

1.2E-3 [-] at 23 °C

ASTM D 150

Dissipation factor, 50Hz

ε''50Hz

5E-4 [-] at 23 °C

IEC 60250 | 50/60 Hz

High Amp Arc Ignition

HAI

3 mm at 23 °C

UL 746A | PLC 3

High Volt Arc Track Rate

HVTR

2 PLC Code at 23 °C

UL 746A | (PLC)

Hot-Wire Ignition

HWI

0.75 mm at 23 °C

UL 746A | PLC 2

Sheet resistivity, ROA

ρel,sheet, ROA

1.00E+15 Ω at 23 °C

IEC 60093

Volume resistivity

ρel, vol

1.00E+17 Ω·cm at 23 °C

ASTM D 257

Rheological Properties

Melt mass-flow rate

MFR

9 g/10min

ASTM D 1238 | 337°C/6.6 kgf

Melt volume-flow rate

MVR

13 cm³/10min

ISO 1133 | MVR at 360°C/5.0 kg

Shrinkage

cshrink

0.5 % at 23 °C

SABIC method | 3.2 mm

Technological properties

Application areas

Additive Plastic, Air Cabin Interiors, Aircraft Seating, Aerospace, Auto Electrical, Circuit Protection, Auto Aftermarket, Audio, Amusement Machine, Animal Testing, Aircraft Exteriors, Defense Vehicles, Displays, Document Handling, Cooking Range, Composite, Commercial Storage/Cookware, Coffee Maker/Espresso Machine, Building Element, Data Management, Data Transfer, Forward Lighting, Food Transportation, Eyeglasses, Furnace/Heater, Fluid Delivery, Food Processor, Fog Lamp, Food Container, Exterior, Electronic Material Handling, Engine Component, Infotainment/Telematic, Industrial Material Handling, Individual Equiptment, Lab Ware and Clinical Diagnostics, Heavy Vehicles, Head Protection, Gear/Bearing/Slider, Enclosures, Enclosure/Housing/Cover, Energy Management, Electronics, Electronic Components, Pharmaceutical Manufacturing, Photo/Video Camera, Pharmaceutical Packaging & Drug Delivery, Power Manangement, Plumbing, Photovoltaic Components, Recreational Vehicle, Refrigerator, Pipe/Fitting, Pump, Rear/Signal Lighting, Rail, Safety Glasses, Respiratory, Security/Detection, Semiconductor, Small Appliance, Sanitary, Servingware, Sensor, Surgical Devices, Personal Care, OLED, Oil/Gas, Non-LED Lighting, Personal Computing, Monitoring and Imaging, Microwave Oven, Meter Gas, Infrastructure, Interior Rail Components, Inverter, Medical Facility Infrastructure, LED Lighting, Medical Device, Wiring Devices, Weapon, Water Treatment/Filtration, Wearables, Wireless Communications, Swimming Pool/Spa, Sunglasses, Surgical Tray, Tray, Vending Machine, Underhood, Washing Machine, Wire & cable, Irrigation

Availability

Europe,Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, General Purpose, High Heat Resistance, Good dimensional stability, Flame Retardant

Filler Type

Processing methods

Middle - Zone 2 Temperature: 340 to 400.0 °C | Drying Temperature: 140 to 150.0 °C | Adapter - Zone 5 Temperature: 330 to 355.0 °C | Nozzle Temperature: 345 to 400.0 °C | Head - Zone 6 - Top Temperature: 330 to 355.0 °C | Drying Temperature: 150 °C | Barrel - Zone 3 Temperature: 330 to 355.0 °C | Melt Temperature: 350 to 400.0 °C | Drying Time (Cumulative): 24 hrs | Front - Zone 3 Temperature: 345 to 400.0 °C | Maximum Moisture Content: 0.02 % | Shot to Cylinder Size: 40 to 60.0 % | Melt Temperature (Parison): 320 to 355.0 °C | Rear - Zone 1 Temperature: 330 to 400.0 °C | Barrel - Zone 2 Temperature: 330 to 355.0 °C | Back Pressure: 0.3 to 0.7 MPa | Screw Speed: 40 to 70.0 rpm | Drying Time: 4 to 6.0 hrs | Barrel - Zone 1 Temperature: 325 to 350.0 °C | Die Temperature: 325 to 355.0 °C | Barrel - Zone 4 Temperature: 330 to 355.0 °C | Maximum Moisture Content: 0.01 to 0.02 % | Vent Depth: 0.025 to 0.076 mm | Mold Temperature: 135 to 165.0 °C | Screw Speed: 10 to 70.0 rpm | Mold Temperature: 65 to 175.0 °C | Drying Time: 4 to 6.0 hrs | Head - Zone 7 - Bottom Temperature: 330 to 355.0 °C | Drying Time (Cumulative): 24 hrs

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.