General
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.41 - 0.57 [-] Show Supplier Material materials with Coefficient of friction of 0.41 - 0.57 [-] | ||
Coefficient of friction, kinetic | 0.57 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.57 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.41 [-] Show Supplier Material materials with Coefficient of friction, static of 0.41 [-] | ASTM D 3702 Modified: Manual | |
Density | 23.0 °C | 1.68 g/cm³ Show Supplier Material materials with Density of 1.68 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.05 % Show Supplier Material materials with Moisture absorption of 0.05 % | ISO 62 | (23°C / 50% RH) |
Water absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Water absorption of 0.1 % | ISO 62-1 | (23°C/24hrs) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10.1 GPa Show Supplier Material materials with Elastic modulus of 10.1 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2.8 % Show Supplier Material materials with Elongation of 2.8 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 8.9 GPa Show Supplier Material materials with Flexural modulus of 8.9 GPa | ISO 178 | 2 mm/min |
Flexural strain | 23.0 °C | 3.1 % Show Supplier Material materials with Flexural strain of 3.1 % | ISO 178 | break, 2 mm/min |
Flexural strength | 23.0 °C | 183 MPa Show Supplier Material materials with Flexural strength of 183 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Impact strength, Izod notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A | notched 80*10*3, -40°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 90 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 90 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched | 23.0 °C | 60 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 60 kJ/m² | ISO 180/1U | unnotched 80*10*4, -40°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 750 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 750 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 13 J Show Supplier Material materials with Instrumented Impact, at Peak of 13 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 114 MPa Show Supplier Material materials with Tensile strength of 114 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3.8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.8E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature | 208 - 222 °C Show Supplier Material materials with Heat deflection temperature of 208 - 222 °C | ||||
Heat deflection temperature, 0.45 MPa | 222 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 222 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 208 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 208 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 75 °C Show Supplier Material materials with Relative temperature index, electrical of 75 °C | UL 746B | |||
Relative temperature index, mechanical impact | 75 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |||
Relative temperature index, mechanical strength | 75 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | |||
Specific heat capacity | 23.0 °C | 1751 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 1751 J/(kg·K) | ASTM E 1269 | ||
Thermal conductivity | 23.0 °C | 0.26 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.26 W/(m·K) | ASTM D 5930 | ||
Vicat softening temperature | 212 °C Show Supplier Material materials with Vicat softening temperature of 212 °C | ISO 306 | Rate B/50 | |||
Flammability | UL Recognized, 94HB Flame Class Rating: 1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101282605- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=103093711- - <br> UL Yellow Card Link 3: https://iq.ul.com/ul/cert.aspx?ULID=101282616- - |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 22 g/10min Show Supplier Material materials with Melt mass-flow rate of 22 g/10min | ASTM D 1238 | 250°C/5.0 kgf | |
Melt volume-flow rate | 17 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 17 cm³/10min | ISO 1133 | MVR at 250°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.1 % Show Supplier Material materials with Shrinkage of 0.1 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage, transverse of 0.5 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Commercial Appliance, Data Management, Data Transfer, Displays, Electronic Components, Electronics, Heavy Vehicles, Gear/Bearing/Slider, Engine Component, Medical Device, Oil/Gas, Personal Computing, Security/Detection, Pharmaceutical Packaging & Drug Delivery, Pallet | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |