General
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.5 - 0.51 [-] Show Supplier Material materials with Coefficient of friction of 0.5 - 0.51 [-] | ||
Coefficient of friction, kinetic | 0.51 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.51 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.5 [-] Show Supplier Material materials with Coefficient of friction, static of 0.5 [-] | ASTM D 3702 Modified: Manual | |
Density | 23.0 °C | 1.24 g/cm³ Show Supplier Material materials with Density of 1.24 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.3 % Show Supplier Material materials with Moisture absorption of 0.3 % | ISO 62 | (23°C / 50% RH) |
Water absorption | 23.0 °C | 0.3 % Show Supplier Material materials with Water absorption of 0.3 % | ISO 62-1 | (23°C/24hrs) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 9 GPa Show Supplier Material materials with Elastic modulus of 9 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 3.2 % Show Supplier Material materials with Elongation of 3.2 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 7.5 GPa Show Supplier Material materials with Flexural modulus of 7.5 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 195 MPa Show Supplier Material materials with Flexural strength of 195 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 17 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 17 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Impact strength, Izod notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 95 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 95 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched | 23.0 °C | 58 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 58 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 800 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 800 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 13 J Show Supplier Material materials with Instrumented Impact, Total Energy of 13 J | ASTM D 3763 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 12 J Show Supplier Material materials with Instrumented Impact, at Peak of 12 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 135 MPa Show Supplier Material materials with Tensile strength of 135 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.9E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.1E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature | 228 - 252 °C Show Supplier Material materials with Heat deflection temperature of 228 - 252 °C | ||||
Heat deflection temperature, 0.45 MPa | 252 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 252 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 228 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 228 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Vicat softening temperature | 185 °C Show Supplier Material materials with Vicat softening temperature of 185 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Recognized, 94HB Flame Class Rating: 1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101344704- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=101282646- - |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 30 g/10min Show Supplier Material materials with Melt mass-flow rate of 30 g/10min | ASTM D 1238 | 300°C/2.16 kgf | |
Melt volume-flow rate | 30 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 30 cm³/10min | ISO 1133 | MVR at 300°C/2.16 kg | |
Shrinkage | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage of 0.2 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 1 % Show Supplier Material materials with Shrinkage, transverse of 1 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Display, Auto Aftermarket, Electronic Components, Gear/Bearing/Slider, Lawn/Garden, Oil/Gas | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |