NORYL GTX™ 810 resin is a 10% glass reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade has high stiffness (flexural modulus 3000 MPa), excellent chemical resistance, and high heat resistance. NORYL GTX GTX810 resin is an excellent candidate for a wide variety of applications including electrical and lighting components, security (CCTV) housings.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.162 g/cm³ Show Supplier Material materials with Density of 1.162 g/cm³	ASTM D 792
Moisture absorption	23.0 °C	1.18 % Show Supplier Material materials with Moisture absorption of 1.18 %	ISO 62 \| (23°C / 50% RH)

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	6 % Show Supplier Material materials with Elongation of 6 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	3.9 GPa Show Supplier Material materials with Flexural modulus of 3.9 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	165 MPa Show Supplier Material materials with Flexural strength of 165 MPa	ISO 178 \| yield, 2 mm/min
Tensile strength	23.0 °C	65 MPa Show Supplier Material materials with Tensile strength of 65 MPa	ISO 527 \| yield, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	4.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 4.4E-5 1/K	ISO 11359-2 \| 23°C to 60°C
Vicat softening temperature		221 °C Show Supplier Material materials with Vicat softening temperature of 221 °C	ISO 306 \| Rate B/50

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.6 % Show Supplier Material materials with Shrinkage of 0.6 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Auto Electrical, Electronic Components, Enclosures, Enclosure/Housing/Cover, Exterior Trim, Forward Lighting, Fixture Bath/Shower, Fog Lamp, Lab Ware and Clinical Diagnostics, Lawn/Garden, Individual Equiptment, Recreational Vehicle, Power Boat, Pipe/Fitting, Rear/Signal Lighting, Photo/Video Camera, Plumbing, Wireless Communications
Availability	Europe,Asia,MEA,Americas
Processing methods	Back Pressure: 0.3 to 1.4MPa Nozzle Temperature: 280 to 305.0°C Maximum Moisture Content: 0.07% Shot to Cylinder Size: 30 to 50.0% Front - Zone 3 Temperature: 275 to 305.0°C Drying Temperature: 95 to 105.0°C Melt Temperature: 280 to 305.0°C Screw Speed: 20 to 100.0rpm Vent Depth: 0.013 to 0.038mm Rear - Zone 1 Temperature: 265 to 305.0°C Middle - Zone 2 Temperature: 270 to 305.0°C Minimum Moisture Content: 0.02% Drying Time: 3 to 4.0hrs Mold Temperature: 75 to 120.0°C Drying Time (Cumulative): 8hrs
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.