LNP™ THERMOCOMP™ Compound LC00APXQ

Want to keep this datasheet? Save it now in your required format

Description

LNP THERMOCOMP LC00APXQ is a compound based on Polyetheretherketone resin containing 50% Carbon Fiber. Added features of this material include: Exceptional Processing, Electrically Conductive.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Moisture absorption

23.0 °C

0.03 %

Show Supplier Material materials with Moisture absorption of 0.03 %

ASTM D 570 | (23°C/50% RH/24 hrs)

Relative density

23.0 °C

1.48 [-]

Show Supplier Material materials with Relative density of 1.48 [-]

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

47.4 GPa

Show Supplier Material materials with Elastic modulus of 47.4 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

1.1 %

Show Supplier Material materials with Elongation of 1.1 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

40.7 GPa

Show Supplier Material materials with Flexural modulus of 40.7 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

473 MPa

Show Supplier Material materials with Flexural strength of 473 MPa

ISO 178

Impact strength, Izod notched

23.0 °C

77 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 77 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

77 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 77 J/m

ASTM D 256 | notched, 23°C

Impact strength, Izod unnotched, ASTM

23.0 °C

768 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 768 J/m

ASTM D 4812 | 23°C

Instrumented Impact, Total Energy

23.0 °C

7 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 7 J

ASTM D 3763 | 23°C

Poisson's ratio

23.0 °C

0.5 [-]

Show Supplier Material materials with Poisson's ratio of 0.5 [-]

ASTM E 132

Shear modulus

23.0 °C

5.2 GPa

Show Supplier Material materials with Shear modulus of 5.2 GPa

ASTM D732

Shear strength

23.0 °C

114 MPa

Show Supplier Material materials with Shear strength of 114 MPa

ASTM D732

Tensile strength

23.0 °C

320 MPa

Show Supplier Material materials with Tensile strength of 320 MPa

ISO 527 | break, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

2E-6 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2E-6 1/K

ASTM E 831 | -40°C to 150°C

Coefficient of thermal expansion, transverse

23.0 °C

2E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 2E-5 1/K

ASTM E 831 | -40°C to 150°C

Heat deflection temperature

335 °C

Show Supplier Material materials with Heat deflection temperature of 335 °C

Heat deflection temperature, 1.80 MPa

335 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 335 °C

ASTM D 648 | 3.2mm, unannealed

Electrical

PropertyTemperatureValueComment

Sheet resistivity, ROA

23.0 °C

100 - 1000 Ω

Show Supplier Material materials with Sheet resistivity, ROA of 100 - 1000 Ω

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.13 %

Show Supplier Material materials with Shrinkage of 0.13 %

ASTM D 955 | 24 hrs

Shrinkage, transverse

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage, transverse of 0.6 %

ASTM D 955 | 24 hrs

Technological properties

Property
Availability

Europe,Asia,Americas

Processing methods

Drying Temperature: 150°C
Drying Time: 4 to 6.0hrs
Front - Zone 3 Temperature: 380 to 400.0°C
Middle - Zone 2 Temperature: 380 to 400.0°C
Rear - Zone 1 Temperature: 370 to 380.0°C
Mold Temperature: 175 to 190.0°C
Back Pressure: 0.3 to 0.7MPa
Screw Speed: 60 to 100.0rpm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.