Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.47 g/cm³ Show Supplier Material materials with Density of 1.47 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.97 % Show Supplier Material materials with Moisture absorption of 0.97 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.5 [-] Show Supplier Material materials with Relative density of 1.5 [-] | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 12.2 GPa Show Supplier Material materials with Elastic modulus of 12.2 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2.7 % Show Supplier Material materials with Elongation of 2.7 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 12.1 GPa Show Supplier Material materials with Flexural modulus of 12.1 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 287 MPa Show Supplier Material materials with Flexural strength of 287 MPa | ISO 178 |
Impact strength, Izod notched | 23.0 °C | 13 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 13 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 117 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 117 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched | 23.0 °C | 74 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 74 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1137 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1137 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 10 J Show Supplier Material materials with Instrumented Impact, Total Energy of 10 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 188 MPa Show Supplier Material materials with Tensile strength of 188 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.68E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.68E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 5.92E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.92E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature | 252 °C Show Supplier Material materials with Heat deflection temperature of 252 °C | ||
Heat deflection temperature, 1.80 MPa | 252 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 252 °C | ASTM D 648 | 3.2mm, unannealed |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Surgical Devices | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |