Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.7 g/cm³ Show Supplier Material materials with Density of 1.7 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 15.7 GPa Show Supplier Material materials with Elastic modulus of 15.7 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2.2 % Show Supplier Material materials with Elongation of 2.2 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 13 GPa Show Supplier Material materials with Flexural modulus of 13 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 264 MPa Show Supplier Material materials with Flexural strength of 264 MPa | ISO 178 | break, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/2C | 23°C |
Impact strength, Charpy unnotched | 23.0 °C | 69 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 69 kJ/m² | ISO 179/2C | 23°C |
Impact strength, Izod notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 123 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 123 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 60 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 60 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 980 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 980 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 172 MPa Show Supplier Material materials with Tensile strength of 172 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.8E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature | 207 °C Show Supplier Material materials with Heat deflection temperature of 207 °C | ||||
Heat deflection temperature, 1.80 MPa | 207 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 207 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 75 °C Show Supplier Material materials with Relative temperature index, electrical of 75 °C | UL 746B | |||
Relative temperature index, mechanical impact | 75 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |||
Relative temperature index, mechanical strength | 75 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | |||
Vicat softening temperature | 215 °C Show Supplier Material materials with Vicat softening temperature of 215 °C | ISO 306 | Rate A/50 | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103376952- - <br> UL Recognized, 94HB Flame Class Rating: ≥0.7mm UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant | 23.0 °C | 3.92 [-] Show Supplier Material materials with Dielectric constant of 3.92 [-] | SABIC method | 1.9 GHz |
Dielectric constant, 1GHz | 23.0 °C | 3.93 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3.93 [-] | SABIC method | 1.1 GHz |
Dissipation factor | 23.0 °C | 7.69E-3 [-] Show Supplier Material materials with Dissipation factor of 7.69E-3 [-] | SABIC method |
Dissipation factor, 1GHz | 23.0 °C | 7.92E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 7.92E-3 [-] | SABIC method | |
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt volume-flow rate | 17 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 17 cm³/10min | ISO 1133 | MVR at 275°C/5 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Electrical Components & Infrastructure | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 100 to 120.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |