General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.635 g/cm³ Show Supplier Material materials with Density of 1.635 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 15.1 GPa Show Supplier Material materials with Elastic modulus of 15.1 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 1.9 % Show Supplier Material materials with Elongation of 1.9 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 13.8 GPa Show Supplier Material materials with Flexural modulus of 13.8 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural strength | 23.0 °C | 223 MPa Show Supplier Material materials with Flexural strength of 223 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Impact strength, Charpy notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Impact strength, Izod notched | 23.0 °C | 127 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 127 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 127 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 127 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 520 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 520 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 21 J Show Supplier Material materials with Instrumented Impact, at Peak of 21 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 153 MPa Show Supplier Material materials with Tensile strength of 153 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.39E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.39E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 4.15E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 4.15E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature | 107 °C Show Supplier Material materials with Heat deflection temperature of 107 °C | ||||
Heat deflection temperature, 1.80 MPa | 107 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 107 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101219669- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥1mm UL 94 <br> UL Recognized, 94V-1 Flame Class Rating: ≥0.8mm UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 5.00E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 5.00E+16 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 2.15E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 2.15E+16 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 48.6 g/10min Show Supplier Material materials with Melt mass-flow rate of 48.6 g/10min | ASTM D 1238 | 300°C/5.0 kgf | |
Melt volume-flow rate | 17 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 17 cm³/10min | ASTM D 1238 | MVR at 300°C/2.16 kg | |
Shrinkage | 23.0 °C | 0.05 % Show Supplier Material materials with Shrinkage of 0.05 % | ASTM D 955 | 24 hrs |
Shrinkage, transverse | 23.0 °C | 0.05 % Show Supplier Material materials with Shrinkage, transverse of 0.05 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing, Wireless Communications, Electronic Components, Heavy Vehicles, Data Transfer | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 110°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |