General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.54 g/cm³ Show Supplier Material materials with Density of 1.54 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 12.5 GPa Show Supplier Material materials with Elastic modulus of 12.5 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 1.7 % Show Supplier Material materials with Elongation of 1.7 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 10.8 GPa Show Supplier Material materials with Flexural modulus of 10.8 GPa | ISO 178 | 2 mm/min |
Flexural strain | 23.0 °C | 1.9 % Show Supplier Material materials with Flexural strain of 1.9 % | ISO 178 | break, 2 mm/min |
Flexural strength | 23.0 °C | 170 MPa Show Supplier Material materials with Flexural strength of 170 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Impact strength, Izod notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 81 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 81 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 22 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 22 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 264 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 264 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 10 J Show Supplier Material materials with Instrumented Impact, at Peak of 10 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 123 MPa Show Supplier Material materials with Tensile strength of 123 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature | 102 - 110 °C Show Supplier Material materials with Heat deflection temperature of 102 - 110 °C | ||
Heat deflection temperature, 0.45 MPa | 110 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 110 °C | ASTM D 648 | 3.2 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 102 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 102 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101343768- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.2mm UL 94 <br> UL Recognized, 94V-1 Flame Class Rating: ≥1mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.5mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.5mm UL 94 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Wireless Communications, Personal Computing, LED Lighting, Data Management | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 110°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |