Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.31 g/cm³ Show Supplier Material materials with Density of 1.31 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 4.8 GPa Show Supplier Material materials with Elastic modulus of 4.8 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 3.8 % Show Supplier Material materials with Elongation of 3.8 % | ISO 527 | break |
Flexural modulus | 23.0 °C | 5 GPa Show Supplier Material materials with Flexural modulus of 5 GPa | ISO 178 |
Flexural strength | 23.0 °C | 158 MPa Show Supplier Material materials with Flexural strength of 158 MPa | ISO 178 |
Impact strength, Izod notched | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 42 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 42 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 33 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 33 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 405 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 405 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 5 J Show Supplier Material materials with Instrumented Impact, at Peak of 5 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 93 MPa Show Supplier Material materials with Tensile strength of 93 MPa | ISO 527 | break |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature | 134 - 140 °C Show Supplier Material materials with Heat deflection temperature of 134 - 140 °C | ||
Heat deflection temperature, 0.45 MPa | 140 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 140 °C | ASTM D 648 | 3.2 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 134 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 134 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101283881- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=101283882- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.64mm UL 94 <br> UV-light, water exposure/immersion: F1- UL 746C |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |