LNP™ THERMOCOMP™ Compound 9X10312

Want to keep this datasheet? Save it now in your required format

Description

9X10312 is 50% glass fiber reinforced, impact modified nylon material. High modulus, high flow and good ductility, Low Moisture Absorption.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Moisture absorption	23.0 °C	0.15 % Show Supplier Material materials with Moisture absorption of 0.15 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.55 [-] Show Supplier Material materials with Relative density of 1.55 [-]	ASTM D 792 \|
Water absorption	23.0 °C	0.8 % Show Supplier Material materials with Water absorption of 0.8 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	15 GPa Show Supplier Material materials with Elastic modulus of 15 GPa	ASTM D 638 \| 5 mm/min
Elongation	23.0 °C	2.8 % Show Supplier Material materials with Elongation of 2.8 %	ASTM D 638 \| brk, Type I, 5 mm/min
Flexural modulus	23.0 °C	13 GPa Show Supplier Material materials with Flexural modulus of 13 GPa	ASTM D 790
Flexural strength	23.0 °C	310 MPa Show Supplier Material materials with Flexural strength of 310 MPa	ASTM D 790
Impact strength, Charpy notched	23.0 °C	16 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 16 kJ/m²	ISO 179/1eA \| V-notch Edgew 80103 sp=62mm, 23°C
Impact strength, Izod notched	23.0 °C	150 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 150 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	150 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 150 J/m	ASTM D 256
Instrumented Impact, Total Energy	23.0 °C	12 J Show Supplier Material materials with Instrumented Impact, Total Energy of 12 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	212 MPa Show Supplier Material materials with Tensile strength of 212 MPa	ASTM D 638 \| brk, Type I, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	250 °C Show Supplier Material materials with Heat deflection temperature of 250 °C
Heat deflection temperature, 1.80 MPa	250 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 250 °C	ASTM D 648 \| 3.2mm, unannealed
Relative temperature index, electrical	65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C	UL 746B
Relative temperature index, mechanical impact	65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C	UL 746B
Relative temperature index, mechanical strength	65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C	UL 746B
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101337256- - <br> UL Recognized, 94HB Flame Class Rating: ≥0.8mm UL 94

Electrical

Property	Temperature	Value	Comment
Dielectric constant, 1GHz	23.0 °C	4 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 4 [-]	ASTM ES 7-83 \| 1.1 GHz
Dissipation factor, 1GHz	23.0 °C	0.01 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 0.01 [-]	ASTM ES 7-83 \| 1.1 GHz

Rheological Properties

Property	Temperature	Value	Comment
Melt volume-flow rate		15 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 15 cm³/10min	ISO 1133 \| MVR at 300°C/2.16 kg
Shrinkage	23.0 °C	0.12 % Show Supplier Material materials with Shrinkage of 0.12 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	0.44 % Show Supplier Material materials with Shrinkage, transverse of 0.44 %	SABIC method \| 3.2 mm

Technological properties

Property
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 80°C Drying Time: 4hrs Maximum Moisture Content: 0.15 to 0.25% Melt Temperature: 280 to 305.0°C Front - Zone 3 Temperature: 295 to 305.0°C Middle - Zone 2 Temperature: 280 to 295.0°C Rear - Zone 1 Temperature: 265 to 275.0°C Mold Temperature: 95 to 110.0°C Back Pressure: 0.2 to 0.3MPa Screw Speed: 30 to 60.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.