LNP™ THERMOCOMP™ Compound DX10311X

Want to keep this datasheet? Save it now in your required format

Description

DX10311X is 30% glass fiber reinforced, impact modified polycarbonate resin. High flow and good ductility.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.43 [-] Show Supplier Material materials with Relative density of 1.43 [-]	ASTM D 792 \|

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	8.6 GPa Show Supplier Material materials with Elastic modulus of 8.6 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	2.5 % Show Supplier Material materials with Elongation of 2.5 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	7.5 GPa Show Supplier Material materials with Flexural modulus of 7.5 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	172 MPa Show Supplier Material materials with Flexural strength of 172 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Charpy notched	23.0 °C	17 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 17 kJ/m²	ISO 179/2C \| 23°C
Impact strength, Charpy unnotched	23.0 °C	45 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 45 kJ/m²	ISO 179/2C \| 23°C
Impact strength, Izod notched	23.0 °C	165 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 165 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	165 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 165 J/m	ASTM D 256 \| notched, 23°C
Impact strength, Izod unnotched, ASTM	23.0 °C	715 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 715 J/m	ASTM D 4812 \| 23°C
Tensile strength	23.0 °C	115 MPa Show Supplier Material materials with Tensile strength of 115 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	2.1E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.1E-5 1/K	ASTM E 831 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	6.8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.8E-5 1/K	ASTM E 831 \| -40°C to 40°C
Heat deflection temperature		125 °C Show Supplier Material materials with Heat deflection temperature of 125 °C
Heat deflection temperature, 0.45 MPa		125 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 125 °C	ASTM D 648 \| 3.2 mm, unannealed

Rheological Properties

Property	Temperature	Value	Comment
Melt volume-flow rate		9 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 9 cm³/10min	ISO 1133 \| MVR at 300°C/2.16 kg
Shrinkage	23.0 °C	0.1 % Show Supplier Material materials with Shrinkage of 0.1 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	0.2 % Show Supplier Material materials with Shrinkage, transverse of 0.2 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Wireless Communications, Personal Computing
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 90 to 110.0°C Drying Time: 3 to 5.0hrs Melt Temperature: 280 to 320.0°C Nozzle Temperature: 280 to 320.0°C Front - Zone 3 Temperature: 280 to 320.0°C Middle - Zone 2 Temperature: 280 to 320.0°C Rear - Zone 1 Temperature: 250 to 280.0°C Mold Temperature: 90 to 120.0°C Back Pressure: 1 to 5.0MPa Screw Speed: 30 to 100.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.