General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.63 g/cm³ Show Supplier Material materials with Density of 1.63 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 1.6 % Show Supplier Material materials with Elongation of 1.6 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 14.8 GPa Show Supplier Material materials with Flexural modulus of 14.8 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 365 MPa Show Supplier Material materials with Flexural strength of 365 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Izod notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod unnotched | 23.0 °C | 65 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 65 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Tensile strength | 23.0 °C | 234 MPa Show Supplier Material materials with Tensile strength of 234 MPa | ISO 527 | yield, 5 mm/min |
Thermal
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.1 % Show Supplier Material materials with Shrinkage of 0.1 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120 to 150.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |