General
Property | Temperature | Value | Comment |
---|---|---|---|
Relative density | 23.0 °C | 1.26 [-] Show Supplier Material materials with Relative density of 1.26 [-] | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10.8 GPa Show Supplier Material materials with Elastic modulus of 10.8 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 2.7 % Show Supplier Material materials with Elongation of 2.7 % | ASTM D 638 | brk, Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 9 GPa Show Supplier Material materials with Flexural modulus of 9 GPa | ASTM D 790 |
Flexural strength | 23.0 °C | 211 MPa Show Supplier Material materials with Flexural strength of 211 MPa | ASTM D 790 |
Impact strength, Izod notched | 23.0 °C | 77 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 77 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 77 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 77 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 588 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 588 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 140 MPa Show Supplier Material materials with Tensile strength of 140 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Thermal
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 1000 - 100000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1000 - 100000 Ω | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 31 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 31 cm³/10min | ISO 1133 | MVR at 300°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.1 % Show Supplier Material materials with Shrinkage of 0.1 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.1 % Show Supplier Material materials with Shrinkage, transverse of 0.1 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Wireless Communications | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 90 to 110.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |