LNP™ LUBRICOMP™ Compound LCL33EXQ

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP LCL33EXQ is a compound based on Polyetheretherketone containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Easy Molding.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Automotive

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Coefficient of friction		0.35 - 0.37 [-] Show Supplier Material materials with Coefficient of friction of 0.35 - 0.37 [-]
Coefficient of friction, kinetic		0.37 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.37 [-]	ASTM D 3702 Modified: Manual
Coefficient of friction, static		0.35 [-] Show Supplier Material materials with Coefficient of friction, static of 0.35 [-]	ASTM D 3702 Modified: Manual
Relative density	23.0 °C	1.45 [-] Show Supplier Material materials with Relative density of 1.45 [-]	ASTM D 792 \|

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	14 GPa Show Supplier Material materials with Elastic modulus of 14 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	1.6 % Show Supplier Material materials with Elongation of 1.6 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	13.5 GPa Show Supplier Material materials with Flexural modulus of 13.5 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	276 MPa Show Supplier Material materials with Flexural strength of 276 MPa	ISO 178
Impact strength, Izod notched	23.0 °C	5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²	ISO 180/1A \| notched 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	69 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 69 J/m	ASTM D 256 \| notched, 23°C
Poisson's ratio	23.0 °C	0.4 [-] Show Supplier Material materials with Poisson's ratio of 0.4 [-]	ISO 527-1/2
Tensile strength	23.0 °C	181 MPa Show Supplier Material materials with Tensile strength of 181 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	320 °C Show Supplier Material materials with Heat deflection temperature of 320 °C
Heat deflection temperature, 1.80 MPa	320 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 320 °C	ASTM D 648 \| 3.2mm, unannealed

Rheological Properties

Property	Value	Comment
Melt volume-flow rate	30 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 30 cm³/10min	ASTM D 1238 \| MVR at 300°C/5.0 kg

Technological properties

Property
Application areas	Heavy Vehicles
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 150°C Drying Time: 4 to 6.0hrs Front - Zone 3 Temperature: 380 to 400.0°C Middle - Zone 2 Temperature: 380 to 400.0°C Rear - Zone 1 Temperature: 370 to 380.0°C Mold Temperature: 175 to 190.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 60 to 100.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.