LNP™ THERMOCOMP™ Compound WF006XXB

Want to keep this datasheet? Save it now in your required format

Description

THERMOCOMP* WF006XXB is a compound based on PBT containing 30% Glass. Added features include: Medium Flow, for use in medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Healthcare

Pharmaceutical Industry

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.53 g/cm³ Show Supplier Material materials with Density of 1.53 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.06 % Show Supplier Material materials with Moisture absorption of 0.06 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.53 [-] Show Supplier Material materials with Relative density of 1.53 [-]	ASTM D 792
Specific volume	23.0 °C	0.66 cm³/g Show Supplier Material materials with Specific volume of 0.66 cm³/g	ASTM D 792
Water absorption	23.0 °C	0.26 % Show Supplier Material materials with Water absorption of 0.26 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	9.3 GPa Show Supplier Material materials with Elastic modulus of 9.3 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	2 % Show Supplier Material materials with Elongation of 2 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	8.5 GPa Show Supplier Material materials with Flexural modulus of 8.5 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	195 MPa Show Supplier Material materials with Flexural strength of 195 MPa	ISO 178 \| yield, 2 mm/min
Hardness, Rockwell R	23.0 °C	118 [-] Show Supplier Material materials with Hardness, Rockwell R of 118 [-]	ASTM D 785
Impact strength, Charpy notched	23.0 °C	5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 5 kJ/m²	ISO 179/1eA \| V-notch Edgew, 23°C, 80104 sp=62mm
Impact strength, Izod notched	23.0 °C	8 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 8 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	85 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 85 J/m	ASTM D 256
Impact strength, Izod unnotched	23.0 °C	45 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 45 kJ/m²	ISO 180/1U \| 80104, 23°C
Impact strength, Izod unnotched, ASTM	23.0 °C	801 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 801 J/m	ASTM D 4812 \| 23°C
Instrumented Impact, Total Energy	23.0 °C	10 J Show Supplier Material materials with Instrumented Impact, Total Energy of 10 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	125 MPa Show Supplier Material materials with Tensile strength of 125 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	2.52E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.52E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	1.2E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature		200 - 215 °C Show Supplier Material materials with Heat deflection temperature of 200 - 215 °C
Heat deflection temperature, 0.45 MPa		215 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C	ASTM D 648 \| 6.4 mm, unannealed
Heat deflection temperature, 1.80 MPa		200 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 200 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Vicat softening temperature		215 °C Show Supplier Material materials with Vicat softening temperature of 215 °C	ISO 306 \| Rate B/50

Electrical

Property	Temperature	Value	Comment
Dielectric constant, 100Hz	23.0 °C	3.8 [-] Show Supplier Material materials with Dielectric constant, 100Hz of 3.8 [-]	ASTM D 150
Dielectric constant, 1MHz	23.0 °C	3.7 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 3.7 [-]	ASTM D 150
Dielectric strength	23.0 °C	24.8 kV/mm Show Supplier Material materials with Dielectric strength of 24.8 kV/mm	ASTM D 149 \| in oil, 1.6 mm
Dissipation factor, 100Hz	23.0 °C	2E-3 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 2E-3 [-]	ASTM D 150
Dissipation factor, 1MHz	23.0 °C	0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-]	ASTM D 150
Volume resistivity	23.0 °C	3.20E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 3.20E+16 Ω·cm	>, ASTM D 257

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		17 g/10min Show Supplier Material materials with Melt mass-flow rate of 17 g/10min	ASTM D 1238 \| 250°C/2.16 kgf
Melt volume-flow rate		13 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 13 cm³/10min	ISO 1133 \| MVR at 250°C/2.16 kg
Shrinkage	23.0 °C	0.5 % Show Supplier Material materials with Shrinkage of 0.5 %
Shrinkage, transverse	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage, transverse of 0.4 %	SABIC method \| 1.5-3.2 mm

Technological properties

Property
Application areas	Pharmaceutical Packaging & Drug Delivery
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 120°C Drying Time: 3 to 4.0hrs Drying Time (Cumulative): 12hrs Maximum Moisture Content: 0.02% Melt Temperature: 250 to 265.0°C Nozzle Temperature: 245 to 260.0°C Front - Zone 3 Temperature: 250 to 265.0°C Middle - Zone 2 Temperature: 245 to 260.0°C Rear - Zone 1 Temperature: 240 to 255.0°C Mold Temperature: 65 to 90.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 50 to 80.0rpm Shot to Cylinder Size: 40 to 80.0% Vent Depth: 0.025 to 0.038mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.