Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of friction | 0.33 - 0.62 [-] Show Supplier Material materials with Coefficient of friction of 0.33 - 0.62 [-] | ||
Coefficient of friction, kinetic | 0.33 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.33 [-] | ASTM D 3702 Modified: Instr. | |
Coefficient of friction, static | 0.62 [-] Show Supplier Material materials with Coefficient of friction, static of 0.62 [-] | ASTM D 3702 Modified: Instr. | |
Density | 23.0 °C | 1.42 g/cm³ Show Supplier Material materials with Density of 1.42 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.4 % Show Supplier Material materials with Water absorption of 0.4 % | ISO 62-1 | (23°C/24hrs) |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 25.1 GPa Show Supplier Material materials with Elastic modulus of 25.1 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 1.3 % Show Supplier Material materials with Elongation of 1.3 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 19.9 GPa Show Supplier Material materials with Flexural modulus of 19.9 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 340 MPa Show Supplier Material materials with Flexural strength of 340 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Izod notched | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 7 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Impact strength, Izod unnotched | 23.0 °C | 40 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 40 kJ/m² | ISO 180/1U | unnotched 80*10*4 |
Tensile strength | 23.0 °C | 256 MPa Show Supplier Material materials with Tensile strength of 256 MPa | ISO 527 | break, 5 mm/min |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 8E-6 1/K | ISO 11359-2 | 23°C to 60°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 5.1E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.1E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Heat deflection temperature | 270 °C Show Supplier Material materials with Heat deflection temperature of 270 °C | ||
Heat deflection temperature, 1.80 MPa | 270 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 270 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 10 - 1000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 10 - 1000 Ω | ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Shrinkage | 23.0 °C | 0.05 % Show Supplier Material materials with Shrinkage of 0.05 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Sensor, Heavy Vehicles, Gear/Bearing/Slider, Lawn/Garden, EV Infrastructure, Electronic Components, Auto Aftermarket | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 120 to 150.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |