LNP™ LUBRICOMP™ Compound XFL36

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP XFL36 is a compound based on Amorphous Nylon containing 30% Glass Fiber and 15% PTFE. Added feature of this material is: Wear Resistant.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Moisture absorption	23.0 °C	0.15 % Show Supplier Material materials with Moisture absorption of 0.15 %	ASTM D 570 \| (23°C/50% RH/24 hrs)
Relative density	23.0 °C	1.47 [-] Show Supplier Material materials with Relative density of 1.47 [-]	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	3 - 4 % Show Supplier Material materials with Elongation of 3 - 4 %	ASTM D 638 \| brk, Type I, 5 mm/min
Flexural modulus	23.0 °C	7.9 GPa Show Supplier Material materials with Flexural modulus of 7.9 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	172 MPa Show Supplier Material materials with Flexural strength of 172 MPa	ASTM D 790 \| brk, 1.3 mm/min, 50 mm span
Impact strength, Izod unnotched, ASTM	23.0 °C	267 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 267 J/m	ASTM D 4812 \| 23°C
Tensile strength	23.0 °C	127 MPa Show Supplier Material materials with Tensile strength of 127 MPa	ASTM D 638 \| brk, Type I, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	137 °C Show Supplier Material materials with Heat deflection temperature of 137 °C
Heat deflection temperature, 1.80 MPa	137 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 137 °C	ASTM D 648 \| 3.2mm, unannealed

Technological properties

Property
Application areas	Electronic Components
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 100 to 120.0°C Drying Time: 6 to 12.0hrs Maximum Moisture Content: 0.1% Melt Temperature: 260 to 300.0°C Front - Zone 3 Temperature: 290 to 300.0°C Middle - Zone 2 Temperature: 270 to 290.0°C Rear - Zone 1 Temperature: 260 to 270.0°C Mold Temperature: 50 to 100.0°C Back Pressure: 0.2 to 0.3MPa Screw Speed: 30 to 60.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.