LNP™ LUBRICOMP™ Compound 5CL23

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP 5CL23 is a compound based on PVDF resin containing 15% Carbon Fiber, 10% PTFE. Added features include: Wear Resistant.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Coefficient of friction

0.44 - 0.53 [-]

Show Supplier Material materials with Coefficient of friction of 0.44 - 0.53 [-]

Coefficient of friction, kinetic

0.53 [-]

Show Supplier Material materials with Coefficient of friction, kinetic of 0.53 [-]

ASTM D 3702 Modified: Manual

Coefficient of friction, static

0.44 [-]

Show Supplier Material materials with Coefficient of friction, static of 0.44 [-]

ASTM D 3702 Modified: Manual

Density

23.0 °C

1.84 g/cm³

Show Supplier Material materials with Density of 1.84 g/cm³

ASTM D 792

Moisture absorption

23.0 °C

0.05 %

Show Supplier Material materials with Moisture absorption of 0.05 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.84 [-]

Show Supplier Material materials with Relative density of 1.84 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

14.5 GPa

Show Supplier Material materials with Elastic modulus of 14.5 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

0.7 %

Show Supplier Material materials with Elongation of 0.7 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

11.9 GPa

Show Supplier Material materials with Flexural modulus of 11.9 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

100 MPa

Show Supplier Material materials with Flexural strength of 100 MPa

ISO 178

Impact strength, Izod notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

55 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 55 J/m

ASTM D 256

Impact strength, Izod unnotched

23.0 °C

13 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 13 kJ/m²

ISO 180/1U | 80*10*4, 23°C

Impact strength, Izod unnotched, ASTM

23.0 °C

201 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 201 J/m

ASTM D 4812 | 23°C

Instrumented Impact, Total Energy

23.0 °C

13 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 13 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

77 MPa

Show Supplier Material materials with Tensile strength of 77 MPa

ISO 527 | break, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

2.1E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2.1E-5 1/K

ASTM D 696 | -30°C to 30°C

Coefficient of thermal expansion, transverse

23.0 °C

8.4E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.4E-5 1/K

ASTM D 696 | -30°C to 30°C

Heat deflection temperature

158 - 166 °C

Show Supplier Material materials with Heat deflection temperature of 158 - 166 °C

Heat deflection temperature, 0.45 MPa

166 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 166 °C

ISO 75/Bf | Flatw 80*10*4 sp=64mm

Heat deflection temperature, 1.80 MPa

158 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 158 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 %

ASTM D 955 | 24 hrs

Shrinkage, transverse

23.0 °C

1 %

Show Supplier Material materials with Shrinkage, transverse of 1 %

ASTM D 955 | 24 hrs

Technological properties

Property
Application areas

Semiconductor

Availability

Europe,Asia,Americas

Processing methods

Drying Temperature: 120 to 150.0°C
Drying Time: 4hrs
Melt Temperature: 215 to 230.0°C
Front - Zone 3 Temperature: 225 to 245.0°C
Middle - Zone 2 Temperature: 210 to 225.0°C
Rear - Zone 1 Temperature: 190 to 210.0°C
Mold Temperature: 65 to 90.0°C
Back Pressure: 0.2 to 0.3MPa
Screw Speed: 30 to 60.0rpm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.