NORYL™ Resin 7310F - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ 7310F resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This FDA Food Contact compliant, injection moldable grade exhibits good surface appearance, high ductility, and good impact resistance along with low moisture absorption, creep resistance, dimensional stability, and hydrolytic stability.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Moisture absorption

23.0 °C

0.04 %

Show Supplier Material materials with Moisture absorption of 0.04 %

ISO 62-4 | (23°C/50% RH/Equilibrium)

Relative density

23.0 °C

1.08 [-]

Show Supplier Material materials with Relative density of 1.08 [-]

ASTM D 792

Water absorption

23.0 °C

0.13 %

Show Supplier Material materials with Water absorption of 0.13 %

ISO 62-1 | (23°C/24hrs)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.1 GPa

Show Supplier Material materials with Elastic modulus of 2.1 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

70 %

Show Supplier Material materials with Elongation of 70 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

2.3 GPa

Show Supplier Material materials with Flexural modulus of 2.3 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

80 MPa

Show Supplier Material materials with Flexural strength of 80 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

13 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m²

ISO 180/1A | notched 80*10*4, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

150 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 150 J/m

ASTM D 256

Impact strength, Izod unnotched

23.0 °C

60 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 60 kJ/m²

ISO 180/1U | unnotched 80*10*4

Impact strength, Izod unnotched, ASTM

23.0 °C

800 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 800 J/m

ASTM D 4812 | 23°C

Instrumented Impact, Total Energy

23.0 °C

55 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 55 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

40 MPa

Show Supplier Material materials with Tensile strength of 40 MPa

ISO 527 | break, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

7.3E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 7.3E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

8.3E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.3E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature

112 °C

Show Supplier Material materials with Heat deflection temperature of 112 °C

Heat deflection temperature, 1.80 MPa

112 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 112 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Relative temperature index, electrical

105 °C

Show Supplier Material materials with Relative temperature index, electrical of 105 °C

UL 746B

Relative temperature index, mechanical impact

90 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 90 °C

UL 746B

Relative temperature index, mechanical strength

105 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C

UL 746B

Vicat softening temperature

135 °C

Show Supplier Material materials with Vicat softening temperature of 135 °C

ISO 306 | Rate B/120

Flammability

UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=228539- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=237006- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

2 V

Show Supplier Material materials with Comparative tracking index of 2 V

UL 746A | (UL) {PLC}

High Amp Arc Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm

≥, UL 746A | PLC 3

High Volt Arc Track Rate

23.0 °C

4 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm

≥, UL 746A | PLC 1

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

11 g/10min

Show Supplier Material materials with Melt mass-flow rate of 11 g/10min

ASTM D 1238 | 280°C/5.0 kgf

Melt volume-flow rate

12 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 12 cm³/10min

ISO 1133 | MVR at 280°C/5.0 kg

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Electronic Components

Availability

Asia

Processing methods

Shot to Cylinder Size: 30 to 70.0%
Drying Temperature: 105 to 110.0°C
Drying Time: 3 to 4.0hrs
Drying Time (Cumulative): 8hrs
Maximum Moisture Content: 0.02%
Melt Temperature: 280 to 310.0°C
Nozzle Temperature: 280 to 310.0°C
Front - Zone 3 Temperature: 270 to 310.0°C
Middle - Zone 2 Temperature: 260 to 305.0°C
Rear - Zone 1 Temperature: 250 to 300.0°C
Mold Temperature: 75 to 105.0°C
Back Pressure: 0.3 to 0.7MPa
Screw Speed: 20 to 100.0rpm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.