Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.33 g/cm³ Show Supplier Material materials with Density of 1.33 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.33 [-] Show Supplier Material materials with Relative density of 1.33 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.2 % Show Supplier Material materials with Water absorption of 0.2 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3 GPa Show Supplier Material materials with Elastic modulus of 3 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 3.2 % Show Supplier Material materials with Elongation of 3.2 % | ISO 527 | yield, 5 mm/min |
Flexural modulus | 23.0 °C | 3.1 GPa Show Supplier Material materials with Flexural modulus of 3.1 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 102 MPa Show Supplier Material materials with Flexural strength of 102 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Impact strength, Izod notched | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 55 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 55 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 39 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 39 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 588 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 588 J/m | ASTM D 4812 | unnotched, -30°C |
Tensile strength | 23.0 °C | 59 MPa Show Supplier Material materials with Tensile strength of 59 MPa | ISO 527 | yield, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5.5E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.4E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature | 98 °C Show Supplier Material materials with Heat deflection temperature of 98 °C | ||||
Heat deflection temperature, 1.80 MPa | 98 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 98 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, mechanical impact | 85 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | |||
Relative temperature index, mechanical strength | 85 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | |||
Vicat softening temperature | 112 °C Show Supplier Material materials with Vicat softening temperature of 112 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101282733- - <br> UL Recognized, 94-5VB Flame Class Rating: ≥2mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 100000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 100000 Ω | ASTM D 257 |
Shielding effectiveness | 23.0 °C | 47 dB Show Supplier Material materials with Shielding effectiveness of 47 dB | SABIC method | @ 3mm |
Volume resistivity | 23.0 °C | 1.00E+7 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+7 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 12.3 g/10min Show Supplier Material materials with Melt mass-flow rate of 12.3 g/10min | ASTM D 1238 | 280°C/5.0 kgf | |
Melt volume-flow rate | 31 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 31 cm³/10min | ISO 1133 | MVR at 265°C/10.0 kg | |
Shrinkage | 23.0 °C | 0.59 % Show Supplier Material materials with Shrinkage of 0.59 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Security/Detection, Personal Computing, Wireless Communications, Enclosures, Electronic Components, Data Transfer, Document Handling, ATM/Ticket Machine | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 85 to 90.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |