NORYL™ Resin EM7304F - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ EM7304F resin is a 15% glass reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade has enhanced polyurethane foam adhesion and high flow along with creep resistance, dimensional stability, and hydrolytic stability. NORYL EM7304F resin is an excellent candidate for automotive interior applications such as instrument panel retainers.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Automotive

General Automotive Parts

Automotive Interior

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.15 [-] Show Supplier Material materials with Relative density of 1.15 [-]	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	2 % Show Supplier Material materials with Elongation of 2 %	ASTM D 638 \| brk, Type I, 5 mm/min
Flexural modulus	23.0 °C	4.6 GPa Show Supplier Material materials with Flexural modulus of 4.6 GPa	ASTM D 790 \| 2.6 mm/min, 100 mm span
Flexural strength	23.0 °C	108 MPa Show Supplier Material materials with Flexural strength of 108 MPa	ASTM D 790 \| yld, 2.6 mm/min, 100 mm span
Impact strength, Izod notched	23.0 °C	64 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 64 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	64 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 64 J/m	ASTM D 256
Tensile strength	23.0 °C	77 MPa Show Supplier Material materials with Tensile strength of 77 MPa	ASTM D 638 \| brk, Type I, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	123 °C Show Supplier Material materials with Heat deflection temperature of 123 °C
Heat deflection temperature, 1.80 MPa	123 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 123 °C	ASTM D 648 \| 6.4 mm, unannealed

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.2 % Show Supplier Material materials with Shrinkage of 0.2 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	0.25 % Show Supplier Material materials with Shrinkage, transverse of 0.25 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Console
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 100 to 105.0°C Drying Time: 3 to 4.0hrs Drying Time (Cumulative): 8hrs Maximum Moisture Content: 0.02% Melt Temperature: 270 to 300.0°C Nozzle Temperature: 270 to 300.0°C Front - Zone 3 Temperature: 260 to 300.0°C Middle - Zone 2 Temperature: 250 to 295.0°C Rear - Zone 1 Temperature: 240 to 290.0°C Mold Temperature: 65 to 95.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 20 to 100.0rpm Shot to Cylinder Size: 30 to 70.0% Vent Depth: 0.038 to 0.051mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.