NORYL PPX™ Resin PPX630F - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL PPX™ 630F resin is a 30% glass reinforced alloy of polyphenylene ether (PPE) + polypropylene (PP). This injection moldable grade is NSF 61 certified and exhibits high elongation and stiffness along with temperature performance, impact resistance, hydrolytic and dimensional stability. NORYL PPX630F resin is an excellent candidate for copper and brass replacement in water management applications such as boiler manifolds, condensers, and hydro blocks.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Construction

Water Management

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.19 [-] Show Supplier Material materials with Relative density of 1.19 [-]	ASTM D 792 \|

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	7.7 % Show Supplier Material materials with Elongation of 7.7 %	ASTM D 638 \| brk, Type I, 5 mm/min
Flexural modulus	23.0 °C	5.6 GPa Show Supplier Material materials with Flexural modulus of 5.6 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	129 MPa Show Supplier Material materials with Flexural strength of 129 MPa	ASTM D 790 \| brk, 1.3 mm/min, 50 mm span
Impact strength, Izod notched	23.0 °C	165 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 165 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	165 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 165 J/m	ASTM D 256
Impact strength, Izod unnotched, ASTM	23.0 °C	827 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 827 J/m	ASTM D 4812 \| 23°C
Instrumented Impact, Total Energy	23.0 °C	20 J Show Supplier Material materials with Instrumented Impact, Total Energy of 20 J	ASTM D 3763 \| -30°C
Tensile strength	23.0 °C	79 MPa Show Supplier Material materials with Tensile strength of 79 MPa	ASTM D 638 \| yld, Type I, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1.44E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.44E-5 1/K	ASTM E 831 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	7.74E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.74E-5 1/K	ASTM E 831 \| -40°C to 40°C
Heat deflection temperature		133 - 155 °C Show Supplier Material materials with Heat deflection temperature of 133 - 155 °C
Heat deflection temperature, 0.45 MPa		155 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 155 °C	ASTM D 648 \| 3.2 mm, unannealed
Heat deflection temperature, 1.80 MPa		133 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 133 °C	ASTM D 648 \| 3.2mm, unannealed
Vicat softening temperature		162 °C Show Supplier Material materials with Vicat softening temperature of 162 °C	ASTM D 1525 \| Rate B/50
Flammability	UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221227- -

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		2.6 g/10min Show Supplier Material materials with Melt mass-flow rate of 2.6 g/10min	ASTM D 1238 \| 260°C/5.0 kgf
Shrinkage	23.0 °C	0.2 % Show Supplier Material materials with Shrinkage of 0.2 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	0.25 % Show Supplier Material materials with Shrinkage, transverse of 0.25 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Pipe/Fitting
Availability	Europe,Asia,Americas
Processing methods	Shot to Cylinder Size: 30 to 70.0% Drying Time (Cumulative): 8hrs Front - Zone 3 Temperature: 255 to 295.0°C Drying Time: 2 to 4.0hrs Mold Temperature: 40 to 65.0°C Drying Temperature: 65 to 75.0°C Nozzle Temperature: 260 to 300.0°C Vent Depth: 0.051 to 0.076mm Screw Speed: 20 to 100.0rpm Maximum Moisture Content: 0.02% Rear - Zone 1 Temperature: 245 to 290.0°C Melt Temperature: 260 to 300.0°C Middle - Zone 2 Temperature: 250 to 290.0°C Back Pressure: 0.3 to 0.7MPa
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.