General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.19 g/cm³ Show Supplier Material materials with Density of 1.19 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 1.8 GPa Show Supplier Material materials with Elastic modulus of 1.8 GPa | ISO 527 | brk, Type I, 5 mm/min |
Elongation | 23.0 °C | 7 % Show Supplier Material materials with Elongation of 7 % | ISO 527 | brk, Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 2 GPa Show Supplier Material materials with Flexural modulus of 2 GPa | ISO 178 | 1.3 mm/min |
Impact strength, Charpy notched | 23.0 °C | 6 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179 | notched, 23°C |
Impact strength, Charpy unnotched | 23.0 °C | 88 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 88 kJ/m² | ISO 179 | un-notched, 23°C |
Impact strength, Izod notched | 23.0 °C | 18 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 18 kJ/m² | ISO 180 | notched, 23°C, |
Impact strength, Izod notched, ASTM | 23.0 °C | 170 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 170 J/m | ASTM D 256 | notched, -30°C |
Impact strength, Izod unnotched | 23.0 °C | 22 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 22 kJ/m² | ISO 180 | un-notched, -30°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1000 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1000 J/m | ASTM D 256 | un-notched, -30°C |
Instrumented Impact, Total Energy | 23.0 °C | 10 J Show Supplier Material materials with Instrumented Impact, Total Energy of 10 J | ASTM D 3763 | -30 °C |
Tensile strength | 23.0 °C | 49 MPa Show Supplier Material materials with Tensile strength of 49 MPa | ISO 527 | brk, Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7.7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.7E-5 1/K | ASTM E 831 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 77 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 77 1/K | ASTM E 831 | ||
Heat deflection temperature | 137 °C Show Supplier Material materials with Heat deflection temperature of 137 °C | ||||
Heat deflection temperature, 1.80 MPa | 137 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 137 °C | ISO 75 | 3.2 mm, unannealed | |||
Vicat softening temperature | 149 °C Show Supplier Material materials with Vicat softening temperature of 149 °C | ISO 306 | Rate A/50 | |||
Flammability | UL94 Flame Class Rating: V-0- UL 94 <br> UL94 Flame Class Rating: V-0- UL 94 <br> UL94 Flame Class Rating: V-2- UL 94 <br> UL94 Flame Class Rating: V-2- UL 94 <br> UL94 Flame Class Rating: V-2- UL 94 <br> UL94 Flame Class Rating: V-2- UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant | 23.0 °C | 2.6 [-] Show Supplier Material materials with Dielectric constant of 2.6 [-] | ASTM D150 |
Dissipation factor | 23.0 °C | 5E-3 [-] Show Supplier Material materials with Dissipation factor of 5E-3 [-] | ASTM D 150 | |
Volume resistivity | 23.0 °C | 1.50E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.50E+15 Ω·cm | ASTM D 257 |
Technological properties
Property | ||
---|---|---|
Application areas | Additive Plastic | |
Availability | Europe,Americas | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |