NORYL PPX™ Resin PPX630 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL PPX™ 630 resin is a 30% glass reinforced alloy of polyphenylene ether (PPE) + polypropylene (PP). This injection moldable grade exhibits high elongation and high stiffness along with temperature performance, impact resistance, hydrolytic and dimensional stability. NORYL PPX630 resin is an excellent candidate for hot water system exteriors, condensate housings, and printer internals. *See NORYL PPX630F resin for NSF 61.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Electronics

Display Devices

Construction

Water Management

Defense

Consumer Goods

Domestic Electrical Appliances

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	7.7 % Show Supplier Material materials with Elongation of 7.7 %	ASTM D 638 \| brk, Type I, 5 mm/min
Flexural modulus	23.0 °C	5.6 GPa Show Supplier Material materials with Flexural modulus of 5.6 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	129 MPa Show Supplier Material materials with Flexural strength of 129 MPa	ASTM D 790 \| brk, 1.3 mm/min, 50 mm span
Impact strength, Izod notched	23.0 °C	165 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 165 kJ/m²	ASTM D 256 \| notched, 23°C
Tensile strength	23.0 °C	79 MPa Show Supplier Material materials with Tensile strength of 79 MPa	ASTM D 638 \| yld, Type I, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1.44E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.44E-5 1/K	ASTM E 831 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	7.74E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.74E-5 1/K	ASTM E 831 \| -40°C to 40°C
Heat deflection temperature		133 - 155 °C Show Supplier Material materials with Heat deflection temperature of 133 - 155 °C
Heat deflection temperature, 0.45 MPa		155 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 155 °C	ASTM D 648 \| 3.2 mm, unannealed
Heat deflection temperature, 1.80 MPa		133 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 133 °C	ASTM D 648 \| 3.2mm, unannealed
Vicat softening temperature		162 °C Show Supplier Material materials with Vicat softening temperature of 162 °C	ASTM D 1525 \| Rate B/50

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.2 % Show Supplier Material materials with Shrinkage of 0.2 %	SABIC method \| on tensile bar
Shrinkage, transverse	23.0 °C	0.25 % Show Supplier Material materials with Shrinkage, transverse of 0.25 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Power Boat, Weapon, Water Treatment/Filtration, Vacuum Cleaner, Furnace/Heater, Hot Water System, Enclosures, Electronic Components, Document Handling
Availability	Europe,Asia,Americas
Processing methods	Middle - Zone 2 Temperature: 250 to 290.0°C Shot to Cylinder Size: 30 to 70.0% Drying Temperature: 65 to 75.0°C Vent Depth: 0.051 to 0.076mm Back Pressure: 0.3 to 0.7MPa Nozzle Temperature: 260 to 300.0°C Mold Temperature: 40 to 65.0°C Drying Time: 2 to 4.0hrs Drying Time (Cumulative): 8hrs Melt Temperature: 260 to 300.0°C Maximum Moisture Content: 0.02% Screw Speed: 20 to 100.0rpm Rear - Zone 1 Temperature: 245 to 290.0°C Front - Zone 3 Temperature: 255 to 295.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.