NORYL™ Resin GFN3F - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ GFN3F resin is a 30% glass reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade exhibits very low moisture absorption, high strength, hydrolytic stability, Low warpage, low specific gravity, and dimensional stability. NORYL GFN3F carries a UL746C outdoor suitability rating of F2 along with FDA food contact compliance and NSF 61 listings in several colors. The properties of this material makes it an excellent candidate for water management applications such as water filter and meter components, pump housings / impellers, shower + faucet, and valves.*See NORYL GFN3 resin for NON FDA / NSF version.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Construction

Water Management

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.29 [-] Show Supplier Material materials with Relative density of 1.29 [-]	ASTM D 792 \|
Water absorption	23.0 °C	0.1 % Show Supplier Material materials with Water absorption of 0.1 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	8.5 GPa Show Supplier Material materials with Elastic modulus of 8.5 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	1.8 % Show Supplier Material materials with Elongation of 1.8 %	ISO 527 \| break
Flexural modulus	23.0 °C	8.7 GPa Show Supplier Material materials with Flexural modulus of 8.7 GPa	ISO 178
Flexural strength	23.0 °C	160 MPa Show Supplier Material materials with Flexural strength of 160 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Charpy notched	23.0 °C	11 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²	ISO 179/2C \| -30°C
Impact strength, Izod notched	23.0 °C	11 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m²	ISO 180/1A \| notched 80104, -30°C
Impact strength, Izod notched, ASTM	23.0 °C	117 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 117 J/m	ASTM D 256
Impact strength, Izod unnotched	23.0 °C	35 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 35 kJ/m²	ISO 180/1U \| unnotched 80104, -30°C
Impact strength, Izod unnotched, ASTM	23.0 °C	588 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 588 J/m	ASTM D 4812 \| 23°C
Tensile strength	23.0 °C	110 MPa Show Supplier Material materials with Tensile strength of 110 MPa	ISO 527 \| break, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	2.3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.3E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature		137 - 143 °C Show Supplier Material materials with Heat deflection temperature of 137 - 143 °C
Heat deflection temperature, 0.45 MPa		143 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 143 °C	ISO 75/Bf \| Flatw 80104 sp=64mm
Heat deflection temperature, 1.80 MPa		137 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 137 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Relative temperature index, electrical		90 °C Show Supplier Material materials with Relative temperature index, electrical of 90 °C	UL 746B
Relative temperature index, mechanical impact		90 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 90 °C	UL 746B
Relative temperature index, mechanical strength		90 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 90 °C	UL 746B
Vicat softening temperature		147 °C Show Supplier Material materials with Vicat softening temperature of 147 °C	ISO 306 \| Rate B/120
Flammability	UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UV-light, water exposure/immersion: F2- UL 746C <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=228546- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=237022- -

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	4 V Show Supplier Material materials with Comparative tracking index of 4 V	UL 746A \| (UL) {PLC}
High Amp Arc Ignition	23.0 °C	1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm	≥, UL 746A \| PLC 4
High Volt Arc Track Rate	23.0 °C	3 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 3 PLC Code	UL 746A \| (PLC)
Hot-Wire Ignition	23.0 °C	1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm	≥, UL 746A \| PLC 0

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		3.2 g/10min Show Supplier Material materials with Melt mass-flow rate of 3.2 g/10min	ASTM D 1238 \| 280°C/5.0 kgf
Melt volume-flow rate		7 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 7 cm³/10min	ISO 1133 \| MVR at 300°C/5.0 kg
Shrinkage	23.0 °C	0.1 % Show Supplier Material materials with Shrinkage of 0.1 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Plumbing, Power Manangement, Pump, Pipe/Fitting, Smart Water Meter, Personal Computing, Meter Water, Wireless Communications, Water Treatment/Filtration, Wearables, Fixture Bath/Shower, Hot Water System
Availability	Americas
Processing methods	Drying Time: 3 to 4.0hrs Shot to Cylinder Size: 30 to 70.0% Rear - Zone 1 Temperature: 265 to 315.0°C Back Pressure: 0.3 to 0.7MPa Nozzle Temperature: 300 to 325.0°C Front - Zone 3 Temperature: 290 to 325.0°C Middle - Zone 2 Temperature: 275 to 320.0°C Mold Temperature: 80 to 110.0°C Melt Temperature: 300 to 325.0°C Drying Time (Cumulative): 8hrs Screw Speed: 20 to 100.0rpm Maximum Moisture Content: 0.02% Drying Temperature: 110 to 120.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.