NORYL™ Resin FE1740PW - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ FE1740PW resin is a 40% glass reinforced blend of polyphenylene ether (PPE) + crystal clear polystyrene (ccPS). This injection moldable material is FC EU, FDA food contact compliant, NSF/ANSI 61*, ACS, WRAS, KTW, and W270 listed for global potable water use. NORYL FE1740PW resin exhibits excellent long-term hydrolytic stability, very low moisture absorption, heat / hot water resistance and is an excellent candidate for a variety of water management applications such as pump housings, impellers, shower/faucet, membrane housings and valves. *NSF certification is color dependent.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Construction

Water Management

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.4 g/cm³ Show Supplier Material materials with Density of 1.4 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.06 % Show Supplier Material materials with Moisture absorption of 0.06 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.4 [-] Show Supplier Material materials with Relative density of 1.4 [-]	ASTM D 792 \|
Water absorption	23.0 °C	0.2 % Show Supplier Material materials with Water absorption of 0.2 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	11.3 GPa Show Supplier Material materials with Elastic modulus of 11.3 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	1.8 % Show Supplier Material materials with Elongation of 1.8 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	9.5 GPa Show Supplier Material materials with Flexural modulus of 9.5 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	195 MPa Show Supplier Material materials with Flexural strength of 195 MPa	ISO 178 \| break, 2 mm/min
Impact strength, Izod notched	23.0 °C	108 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 108 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	90 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 90 J/m	ASTM D 256
Impact strength, Izod unnotched	23.0 °C	30 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 30 kJ/m²	ISO 180/1U \| unnotched 80104, -30°C
Instrumented Impact, Total Energy	23.0 °C	18 J Show Supplier Material materials with Instrumented Impact, Total Energy of 18 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	155 MPa Show Supplier Material materials with Tensile strength of 155 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	2E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature		147 °C Show Supplier Material materials with Heat deflection temperature of 147 °C
Heat deflection temperature, 1.80 MPa		147 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 147 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Vicat softening temperature		152 °C Show Supplier Material materials with Vicat softening temperature of 152 °C	ISO 306 \| Rate B/50

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		10 g/10min Show Supplier Material materials with Melt mass-flow rate of 10 g/10min	ASTM D 1238 \| 300°C/5.0 kgf
Melt volume-flow rate		20 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 20 cm³/10min	ISO 1133 \| MVR at 300°C/10.0 kg
Shrinkage	23.0 °C	0.09 % Show Supplier Material materials with Shrinkage of 0.09 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Pump, Pipe/Fitting
Availability	Europe,Asia,Americas
Processing methods	Mold Temperature: 80 to 120.0°C Drying Time: 2 to 4.0hrs Middle - Zone 2 Temperature: 270 to 290.0°C Rear - Zone 1 Temperature: 250 to 270.0°C Melt Temperature: 280 to 300.0°C Nozzle Temperature: 280 to 300.0°C Front - Zone 3 Temperature: 290 to 310.0°C Hopper Temperature: 60 to 80.0°C Drying Temperature: 100 to 120.0°C Maximum Moisture Content: 0.02%
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.