General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.3 g/cm³ Show Supplier Material materials with Density of 1.3 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.06 % Show Supplier Material materials with Moisture absorption of 0.06 % | ISO 62 | (23°C / 50% RH) |
Water absorption | 23.0 °C | 0.2 % Show Supplier Material materials with Water absorption of 0.2 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 9.6 GPa Show Supplier Material materials with Elastic modulus of 9.6 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2.5 % Show Supplier Material materials with Elongation of 2.5 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 8.1 GPa Show Supplier Material materials with Flexural modulus of 8.1 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 192 MPa Show Supplier Material materials with Flexural strength of 192 MPa | ISO 178 | break, 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 240 MPa Show Supplier Material materials with Hardness, Ball Indentation of 240 MPa | ISO 2039-1 | H358/30 |
Impact strength, Charpy notched | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Impact strength, Charpy unnotched | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 30 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Impact strength, Izod notched | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 7 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 75 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 75 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 30 kJ/m² | ISO 180/1U | unnotched 80*10*4, -30°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 505 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 505 J/m | ASTM D 4812 | 23°C |
Taber Abrasion | 23.0 °C | 65 mg/1000cy Show Supplier Material materials with Taber Abrasion of 65 mg/1000cy | SABIC method | CS-17, 1 kg |
Tensile strength | 23.0 °C | 133 MPa Show Supplier Material materials with Tensile strength of 133 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature | 145 - 150 °C Show Supplier Material materials with Heat deflection temperature of 145 - 150 °C | ||
Heat deflection temperature, 0.45 MPa | 150 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 150 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |
Heat deflection temperature, 1.80 MPa | 145 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 145 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |
Vicat softening temperature | 158 °C Show Supplier Material materials with Vicat softening temperature of 158 °C | ISO 306 | Rate B/120 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 9 g/10min Show Supplier Material materials with Melt mass-flow rate of 9 g/10min | ASTM D 1238 | 300°C/5.0 kgf | |
Melt volume-flow rate | 30 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 30 cm³/10min | ISO 1133 | MVR at 300°C/10.0 kg | |
Shrinkage | 23.0 °C | 0.1 % Show Supplier Material materials with Shrinkage of 0.1 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage, transverse of 0.2 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Vending Machine, Water Treatment/Filtration, Meter Water, Smart Water Meter, Small Appliance, Plumbing, Pipe/Fitting, Pump, Heavy Vehicles, Hot Water System, Fixture Bath/Shower, Electronic Components, Coffee Maker/Espresso Machine | |
Availability | Europe,Asia,MEA,Americas | |
Processing methods | Maximum Moisture Content: 0.02% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |