NORYL™ Resin FE1630PW - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ FE1630PW resin is a 30% glass reinforced blend of polyphenylene ether (PPE) + crystal clear polystyrene (ccPS). This injection moldable material is FC EU, FDA food contact compliant, NSF/ANSI 61*ACS, WRAS, KTW, and W270 listed for global potable water use. NORYL FE1630PW resin exhibits excellent long-term hydrolytic stability, very low moisture absorption, heat / hot water resistance and is an excellent candidate for a variety of water management applications such as pump housings, impellers, shower/faucet, membrane housings and valves. *NSF certification is color dependent.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Automotive

Construction

Water Management

Consumer Goods

Domestic Electrical Appliances

General Appliances

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.3 g/cm³ Show Supplier Material materials with Density of 1.3 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.06 % Show Supplier Material materials with Moisture absorption of 0.06 %	ISO 62 \| (23°C / 50% RH)
Water absorption	23.0 °C	0.2 % Show Supplier Material materials with Water absorption of 0.2 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	9.6 GPa Show Supplier Material materials with Elastic modulus of 9.6 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	2.5 % Show Supplier Material materials with Elongation of 2.5 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	8.1 GPa Show Supplier Material materials with Flexural modulus of 8.1 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	192 MPa Show Supplier Material materials with Flexural strength of 192 MPa	ISO 178 \| break, 2 mm/min
Hardness, Ball Indentation	23.0 °C	240 MPa Show Supplier Material materials with Hardness, Ball Indentation of 240 MPa	ISO 2039-1 \| H358/30
Impact strength, Charpy notched	23.0 °C	10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²	ISO 179/1eA \| V-notch Edgew 80104 sp=62mm, 23°C
Impact strength, Charpy unnotched	23.0 °C	30 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 30 kJ/m²	ISO 179/1eU \| Unnotch Edgew 80104 sp=62mm, -30°C
Impact strength, Izod notched	23.0 °C	8 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 8 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	85 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 85 J/m	ASTM D 256
Impact strength, Izod unnotched	23.0 °C	30 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 30 kJ/m²	ISO 180/1U \| unnotched 80104
Impact strength, Izod unnotched, ASTM	23.0 °C	505 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 505 J/m	ASTM D 4812 \| 23°C
Taber Abrasion	23.0 °C	65 mg/1000cy Show Supplier Material materials with Taber Abrasion of 65 mg/1000cy	SABIC method \| CS-17, 1 kg
Tensile strength	23.0 °C	133 MPa Show Supplier Material materials with Tensile strength of 133 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature		145 - 150 °C Show Supplier Material materials with Heat deflection temperature of 145 - 150 °C
Heat deflection temperature, 0.45 MPa		150 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 150 °C	ISO 75/Be \| Edgew 120104 sp=100mm
Heat deflection temperature, 1.80 MPa		145 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 145 °C	ISO 75/Ae \| Edgew 120104 sp=100mm
Vicat softening temperature		154 °C Show Supplier Material materials with Vicat softening temperature of 154 °C	ISO 306 \| Rate B/50

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		9 g/10min Show Supplier Material materials with Melt mass-flow rate of 9 g/10min	ASTM D 1238 \| 300°C/5.0 kgf
Melt volume-flow rate		30 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 30 cm³/10min	ISO 1133 \| MVR at 300°C/10.0 kg
Shrinkage	23.0 °C	0.1 % Show Supplier Material materials with Shrinkage of 0.1 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	0.2 % Show Supplier Material materials with Shrinkage, transverse of 0.2 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Vending Machine, Water Treatment/Filtration, Meter Water, Smart Water Meter, Small Appliance, Plumbing, Pipe/Fitting, Pump, Heavy Vehicles, Hot Water System, Fixture Bath/Shower, Electronic Components, Coffee Maker/Espresso Machine
Availability	Europe,Asia,MEA,Americas
Processing methods	Nozzle Temperature: 290 to 320.0°C Front - Zone 3 Temperature: 300 to 310.0°C Melt Temperature: 290 to 320.0°C Mold Temperature: 80 to 120.0°C Hopper Temperature: 60 to 80.0°C Drying Time: 2 to 4.0hrs Maximum Moisture Content: 0.02% Rear - Zone 1 Temperature: 270 to 280.0°C Middle - Zone 2 Temperature: 280 to 300.0°C Drying Temperature: 100 to 120.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.