General
Property | Temperature | Value | Comment |
---|---|---|---|
Relative density | 23.0 °C | 1.39 [-] Show Supplier Material materials with Relative density of 1.39 [-] | ASTM D 792 | |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 6.9 GPa Show Supplier Material materials with Elastic modulus of 6.9 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 3 % Show Supplier Material materials with Elongation of 3 % | ASTM D 638 | yld, Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 6.9 GPa Show Supplier Material materials with Flexural modulus of 6.9 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural strength | 23.0 °C | 206 MPa Show Supplier Material materials with Flexural strength of 206 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Impact strength, Izod notched | 23.0 °C | 80 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 80 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 80 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 80 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 587 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 587 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 14 J Show Supplier Material materials with Instrumented Impact, Total Energy of 14 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 137 MPa Show Supplier Material materials with Tensile strength of 137 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.6E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7.2E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.2E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature | 206 - 211 °C Show Supplier Material materials with Heat deflection temperature of 206 - 211 °C | ||||
Heat deflection temperature, 0.45 MPa | 211 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 211 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 206 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 206 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Vicat softening temperature | 210 °C Show Supplier Material materials with Vicat softening temperature of 210 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94V-0 Flame Class Rating: ≥0.4mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221095- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=221096- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 4 V Show Supplier Material materials with Comparative tracking index of 4 V | UL 746A | (UL) {PLC} |
High Amp Arc Ignition | 23.0 °C | 0.4 mm Show Supplier Material materials with High Amp Arc Ignition of 0.4 mm | ≥, UL 746A | PLC 4 |
High Volt Arc Track Rate | 23.0 °C | 4 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 0.75 mm Show Supplier Material materials with Hot-Wire Ignition of 0.75 mm | ≥, UL 746A | PLC 3 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 13 g/10min Show Supplier Material materials with Melt mass-flow rate of 13 g/10min | ASTM D 1238 | 337°C/6.6 kgf | |
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage, transverse of 0.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components, Enclosure/Housing/Cover, Circuit Protection, Semiconductor, Personal Computing, Wire & cable | |
Availability | Asia,Americas | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |