NORYL™ Resin NHP9023 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ NHP9023 resin is a 15% glass reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 1.5mm and V1 at 0.75mm for thin-wall molding capability. NORYL NHP9023 is based on a unique co-polymer technology and exhibits good dimensional stability, high heat resistance, strong electrical performance, and very low specific gravity. It is an excellent candidate for copier fuser units, business equipment internal components, and electrical applications where thin-wall FR, modulus retention, and high heat resistance are required.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.21 g/cm³ Show Supplier Material materials with Density of 1.21 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.11 % Show Supplier Material materials with Moisture absorption of 0.11 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.21 [-] Show Supplier Material materials with Relative density of 1.21 [-]	ASTM D 792
Water absorption	23.0 °C	0.2 % Show Supplier Material materials with Water absorption of 0.2 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	5.5 GPa Show Supplier Material materials with Elastic modulus of 5.5 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	2.7 % Show Supplier Material materials with Elongation of 2.7 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	5.2 GPa Show Supplier Material materials with Flexural modulus of 5.2 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	163 MPa Show Supplier Material materials with Flexural strength of 163 MPa	ISO 178 \| yield, 2 mm/min
Hardness, Rockwell R	23.0 °C	121 [-] Show Supplier Material materials with Hardness, Rockwell R of 121 [-]	ASTM D 785
Impact strength, Charpy notched	23.0 °C	7 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m²	ISO 179/1eA \| V-notch Edgew, 23°C, 80104 sp=62mm
Impact strength, Izod notched	23.0 °C	7 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 7 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	72 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 72 J/m	ASTM D 256
Impact strength, Izod unnotched	23.0 °C	28 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 28 kJ/m²	ISO 180/1U \| unnotched 80104, -30°C
Tensile strength	23.0 °C	90 MPa Show Supplier Material materials with Tensile strength of 90 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	3.8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.8E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	6.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.4E-5 1/K	ISO 11359-2 \| 23°C to 80°C
Heat deflection temperature		153 °C Show Supplier Material materials with Heat deflection temperature of 153 °C
Heat deflection temperature, 1.80 MPa		153 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 153 °C	ASTM D 648 \| 6.4 mm, unannealed
Vicat softening temperature		163 °C Show Supplier Material materials with Vicat softening temperature of 163 °C	ISO 306 \| Rate B/120
Flammability	UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-1 Flame Class Rating: ≥0.75mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102131113- -

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	175 V Show Supplier Material materials with Comparative tracking index of 175 V	IEC 60112 \|

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		20 g/10min Show Supplier Material materials with Melt mass-flow rate of 20 g/10min	ASTM D 1238 \| 300°C/5.0 kgf
Shrinkage	23.0 °C	0.38 % Show Supplier Material materials with Shrinkage of 0.38 %	SABIC method \| on tensile bar

Technological properties

Property
Application areas	Document Handling
Availability	Europe,Asia,Americas
Processing methods	Mold Temperature: 80 to 110.0°C Maximum Moisture Content: 0.02% Rear - Zone 1 Temperature: 265 to 315.0°C Middle - Zone 2 Temperature: 275 to 320.0°C Drying Time: 3 to 4.0hrs Melt Temperature: 300 to 325.0°C Shot to Cylinder Size: 30 to 70.0% Drying Temperature: 110 to 120.0°C Front - Zone 3 Temperature: 290 to 325.0°C Drying Time (Cumulative): 8hrs Screw Speed: 20 to 100.0rpm Nozzle Temperature: 300 to 325.0°C Back Pressure: 0.3 to 0.7MPa
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.