General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.44 g/cm³ Show Supplier Material materials with Density of 1.44 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.07 % Show Supplier Material materials with Moisture absorption of 0.07 % | 23°C/50% |
Relative density | 23.0 °C | 1.44 [-] Show Supplier Material materials with Relative density of 1.44 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.2 % Show Supplier Material materials with Water absorption of 0.2 % | ISO 62-1 | (23°C/24hrs) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 8.9 GPa Show Supplier Material materials with Elastic modulus of 8.9 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 3 % Show Supplier Material materials with Elongation of 3 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 7.2 GPa Show Supplier Material materials with Flexural modulus of 7.2 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 197 MPa Show Supplier Material materials with Flexural strength of 197 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Impact strength, Izod notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 89 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 89 J/m | ASTM D 256 |
Tensile strength | 23.0 °C | 157 MPa Show Supplier Material materials with Tensile strength of 157 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.8E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 5.9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.9E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Heat deflection temperature | 208 °C Show Supplier Material materials with Heat deflection temperature of 208 °C | ||||
Heat deflection temperature, 1.80 MPa | 208 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 208 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100116343- - |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 19.7 g/10min Show Supplier Material materials with Melt mass-flow rate of 19.7 g/10min | ASTM D 1238 | 337°C/6.6 kgf | |
Melt volume-flow rate | 40 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 40 cm³/10min | ISO 1133 | MVR at 345°C/10.0 kg | |
Shrinkage | 23.0 °C | 0.46 % Show Supplier Material materials with Shrinkage of 0.46 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 0.54 % Show Supplier Material materials with Shrinkage, transverse of 0.54 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Photo/Video Camera, Semiconductor, Electronic Components, Circuit Protection, Additive Semiconductor Materials | |
Availability | Europe,Asia,Americas | |
Processing methods | Shot to Cylinder Size: 40 to 60.0% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |