General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.2 g/cm³ Show Supplier Material materials with Density of 1.2 g/cm³ | ISO 1183 |
Limiting oxygen index | 23.0 °C | 48 % Show Supplier Material materials with Limiting oxygen index of 48 % | |
Relative density | 23.0 °C | 1.2 [-] Show Supplier Material materials with Relative density of 1.2 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.76 % Show Supplier Material materials with Water absorption of 0.76 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 15 % Show Supplier Material materials with Elongation of 15 % | ISO 527 | break, 50 mm/min |
Flexural modulus | 23.0 °C | 2 GPa Show Supplier Material materials with Flexural modulus of 2 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 98 MPa Show Supplier Material materials with Flexural strength of 98 MPa | ISO 178 | yield, 2 mm/min |
Hardness, Shore D | 23.0 °C | 80 [-] Show Supplier Material materials with Hardness, Shore D of 80 [-] | ASTM D 2240 |
Impact strength, Izod notched | 23.0 °C | 16 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 16 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Taber Abrasion | 23.0 °C | 50 mg/1000cy Show Supplier Material materials with Taber Abrasion of 50 mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
Tear strength | 23.0 °C | 37 kN/m Show Supplier Material materials with Tear strength of 37 kN/m | ISO 34 (Method A) | @ 1.6mm |
Tensile strength | 23.0 °C | 68 MPa Show Supplier Material materials with Tensile strength of 68 MPa | ISO 527 | yield, 50 mm/min |
Thermal
Property | Value | Comment | |
---|---|---|---|
Glass transition temperature | 200 °C Show Supplier Material materials with Glass transition temperature of 200 °C | DMA | matrix | |
Heat deflection temperature | 164 °C Show Supplier Material materials with Heat deflection temperature of 164 °C | ||
Heat deflection temperature, 0.45 MPa | 164 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 164 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Vicat softening temperature | 180 °C Show Supplier Material materials with Vicat softening temperature of 180 °C | ISO 306 | Rate B/120 | |
Flammability | UL Compliant, 94V-0 Flame Class Rating: 1.6mm UL 94 by SABIC-IP |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 100Hz | 23.0 °C | 3.13 [-] Show Supplier Material materials with Dielectric constant, 100Hz of 3.13 [-] | ASTM D 150 |
Dielectric constant, 1KHz | 23.0 °C | 3 [-] Show Supplier Material materials with Dielectric constant, 1KHz of 3 [-] | ASTM D 150 |
Dielectric constant, 1MHz | 23.0 °C | 3.04 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 3.04 [-] | ASTM D 150 |
Dielectric strength | 23.0 °C | 16.7 kV/mm Show Supplier Material materials with Dielectric strength of 16.7 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 0.01 [-] | ASTM D 150 |
Dissipation factor, 100kHz | 23.0 °C | 6.1E-3 [-] Show Supplier Material materials with Dissipation factor, 100kHz of 6.1E-3 [-] | ASTM D 150 |
Dissipation factor, 1MHz | 23.0 °C | 5.4E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 5.4E-3 [-] | ASTM D 150 |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, ASTM D 257 |
Volume resistivity | 23.0 °C | 1.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 Ω·cm | >, ASTM D 257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Document Handling, Composite, Adhesives | |
Availability | Europe,Americas | |
Processing methods | Drying Time (Cumulative): 8hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |