Property | Temperature | Value | Comment |
---|---|---|---|
Relative density | 23.0 °C | 1.1 [-] Show Supplier Material materials with Relative density of 1.1 [-] | ASTM D 792 | |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 14 % Show Supplier Material materials with Elongation of 14 % | ASTM D 638 | brk, Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.5 GPa Show Supplier Material materials with Flexural modulus of 2.5 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Flexural strength | 23.0 °C | 100 MPa Show Supplier Material materials with Flexural strength of 100 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Impact strength, Izod notched | 23.0 °C | 180 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 180 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 180 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 180 J/m | ASTM D 256 |
Tensile strength | 23.0 °C | 73 MPa Show Supplier Material materials with Tensile strength of 73 MPa | ASTM D 638 | yld, Type I, 50 mm/min |
Thermal
Property | Value | Comment | |
---|---|---|---|
Ball pressure temperature | 120 °C Show Supplier Material materials with Ball pressure temperature of 120 °C | IEC 60695-10-2 | approximate maximum | |
Heat deflection temperature | 118 °C Show Supplier Material materials with Heat deflection temperature of 118 °C | ||
Heat deflection temperature, 1.80 MPa | 118 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 118 °C | ASTM D 648 | 6.4 mm, unannealed | |
Relative temperature index, electrical | 125 °C Show Supplier Material materials with Relative temperature index, electrical of 125 °C | UL 746B | |
Relative temperature index, mechanical impact | 125 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 125 °C | UL 746B | |
Relative temperature index, mechanical strength | 125 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 125 °C | UL 746B | |
Flammability | UL Recognized, 94V-0 Flame Class Rating: ≥0.75mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100850147- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 2 V Show Supplier Material materials with Comparative tracking index of 2 V | UL 746A | (UL) {PLC} |
Dielectric strength | 23.0 °C | 27 kV/mm Show Supplier Material materials with Dielectric strength of 27 kV/mm | ASTM D 149 | in air, 3.2 mm |
Hot-Wire Ignition | 23.0 °C | 3 mm Show Supplier Material materials with Hot-Wire Ignition of 3 mm | ≥, UL 746A | PLC 1 |
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt mass-flow rate | 5 g/10min Show Supplier Material materials with Melt mass-flow rate of 5 g/10min | ASTM D 1238 | 250°C/10.0 kgf |
Technological properties
Property | ||
---|---|---|
Availability | Asia | |
Processing methods | Screw Speed: 20 to 100.0rpm | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |