NORYL™ Resin PX9406K - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL PX9406K resin may be suitable for consumer electronics applications. Flame retardant used is non-halogenated. UL94 V0 at 1.5 mm, 5VB at 2 mm, and 5VA at 2.5 mm. RTI (impact) = 105 C

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Construction

Consumer Goods

Domestic Electrical Appliances

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.1 g/cm³ Show Supplier Material materials with Density of 1.1 g/cm³	ISO 1183
Relative density	23.0 °C	1.1 [-] Show Supplier Material materials with Relative density of 1.1 [-]	ASTM D 792 \|

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.6 GPa Show Supplier Material materials with Elastic modulus of 2.6 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	5 % Show Supplier Material materials with Elongation of 5 %	ISO 527 \| yield, 50 mm/min
Flexural modulus	23.0 °C	2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	104 MPa Show Supplier Material materials with Flexural strength of 104 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Charpy notched	23.0 °C	5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 5 kJ/m²	ISO 179/1eA \| V-notch Edgew 80104 sp=62mm, -30°C
Impact strength, Izod notched	23.0 °C	5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²	ISO 180/1A \| notched 80104, -30°C
Impact strength, Izod notched, ASTM	23.0 °C	170 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 170 J/m	ASTM D 256
Instrumented Impact, Total Energy	23.0 °C	55 J Show Supplier Material materials with Instrumented Impact, Total Energy of 55 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	67 MPa Show Supplier Material materials with Tensile strength of 67 MPa	ISO 527 \| yield, 50 mm/min

Thermal

Property	Value	Comment
Ball Pressure Test	nan	IEC 60695-10-2 \| 125°C +/- 2°C
Glow Wire Flammability Index	960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C
Glow Wire Ignition Temperature	800 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 800 °C	IEC 60695-2-13 \| 2.0 mm
Heat deflection temperature	111 - 128 °C Show Supplier Material materials with Heat deflection temperature of 111 - 128 °C
Heat deflection temperature, 0.45 MPa	128 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 128 °C	ASTM D 648 \| 3.2 mm, unannealed
Heat deflection temperature, 1.80 MPa	111 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 111 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Relative temperature index, electrical	110 °C Show Supplier Material materials with Relative temperature index, electrical of 110 °C	UL 746B
Relative temperature index, mechanical impact	105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C	UL 746B
Relative temperature index, mechanical strength	110 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 110 °C	UL 746B
Vicat softening temperature	144 °C Show Supplier Material materials with Vicat softening temperature of 144 °C	ISO 306 \| Rate A/120
Flammability	Glow Wire Ignitability Temperature, 1.5 mm: 800°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101401128- - <br> UL Recognized, 94-5VA Flame Class Rating: ≥2.5mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94-5VB Flame Class Rating: ≥2mm UL 94

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	2 V Show Supplier Material materials with Comparative tracking index of 2 V	UL 746A \| (UL) {PLC}
Dielectric strength	23.0 °C	49 kV/mm Show Supplier Material materials with Dielectric strength of 49 kV/mm	ASTM D 149 \| in air, 3.2 mm
High Amp Arc Ignition	23.0 °C	1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm	≥, UL 746A \| PLC 0
High Volt Arc Track Rate	23.0 °C	3 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 3 PLC Code	UL 746A \| (PLC)
Hot-Wire Ignition	23.0 °C	1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm	≥, UL 746A \| PLC 0
Volume resistivity	23.0 °C	1.40E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 1.40E+17 Ω·cm	ASTM D 257

Rheological Properties

Property	Temperature	Value	Comment
Melt viscosity	23.0 °C	250 Pa·s Show Supplier Material materials with Melt viscosity of 250 Pa·s	ISO 11443 \| 280°C, 1500 sec-1
Melt volume-flow rate		7 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 7 cm³/10min	ISO 1133 \| MVR at 250°C/10.0 kg

Technological properties

Property
Application areas	Refrigerator, Washing Machine, Air Conditioning, Gas/Electric Oven, Enclosure/Housing/Cover
Availability	Asia
Processing methods	Middle - Zone 2 Temperature: 255 to 300.0°C Back Pressure: 0.3 to 0.7MPa Rear - Zone 1 Temperature: 245 to 295.0°C Mold Temperature: 70 to 100.0°C Vent Depth: 0.038 to 0.051mm Nozzle Temperature: 275 to 305.0°C Shot to Cylinder Size: 30 to 70.0% Drying Time: 3 to 4.0hrs Drying Time (Cumulative): 8hrs Melt Temperature: 275 to 305.0°C Drying Temperature: 105 to 110.0°C Screw Speed: 20 to 100.0rpm Maximum Moisture Content: 0.02% Front - Zone 3 Temperature: 265 to 305.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.