General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.3 g/cm³ Show Supplier Material materials with Density of 1.3 g/cm³ | ISO 1183 |
Limiting oxygen index | 23.0 °C | 26 % Show Supplier Material materials with Limiting oxygen index of 26 % | |
Moisture absorption | 23.0 °C | 0.06 % Show Supplier Material materials with Moisture absorption of 0.06 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.29 [-] Show Supplier Material materials with Relative density of 1.29 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.2 % Show Supplier Material materials with Water absorption of 0.2 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 8.1 GPa Show Supplier Material materials with Elastic modulus of 8.1 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2 % Show Supplier Material materials with Elongation of 2 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 7.1 GPa Show Supplier Material materials with Flexural modulus of 7.1 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 170 MPa Show Supplier Material materials with Flexural strength of 170 MPa | ISO 178 | break, 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 130 MPa Show Supplier Material materials with Hardness, Ball Indentation of 130 MPa | ISO 2039-1 | H358/30 |
Impact strength, Izod notched | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Impact strength, Izod unnotched | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 30 kJ/m² | ISO 180/1U | unnotched 80*10*4, -30°C |
Taber Abrasion | 23.0 °C | 70 mg/1000cy Show Supplier Material materials with Taber Abrasion of 70 mg/1000cy | SABIC method | CS-17, 1 kg |
Tensile strength | 23.0 °C | 106 MPa Show Supplier Material materials with Tensile strength of 106 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coefficient of thermal expansion | 23.0 °C | 2E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Glow Wire Ignition Temperature | 750 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 750 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature | 140 - 145 °C Show Supplier Material materials with Heat deflection temperature of 140 - 145 °C | ||||
Heat deflection temperature, 0.45 MPa | 145 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 145 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 140 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 140 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Vicat softening temperature | 158 °C Show Supplier Material materials with Vicat softening temperature of 158 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Flammability Index 750°C, passes at: 3mm IEC 60695-2-12 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103460844- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 1MHz | 23.0 °C | 2.9 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 2.9 [-] | IEC 60250 |
Dielectric constant, 60Hz | 23.0 °C | 2.9 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 2.9 [-] | IEC 60250 | 50/60 Hz |
Dielectric strength | 23.0 °C | 18 kV/mm Show Supplier Material materials with Dielectric strength of 18 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Dissipation factor, 1MHz | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 1E-3 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 6E-4 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 6E-4 [-] | IEC 60250 | 50/60 Hz |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, IEC 60093 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 60093 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 16 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 16 cm³/10min | ISO 1133 | MVR at 300°C/10.0 kg | |
Shrinkage | 23.0 °C | 0.1 % Show Supplier Material materials with Shrinkage of 0.1 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage, transverse of 0.2 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Hydroblocks | |
Availability | Europe | |
Processing methods | Mold Temperature: 80 to 120.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |