General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.275 g/cm³ Show Supplier Material materials with Density of 1.275 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.8 GPa Show Supplier Material materials with Elastic modulus of 2.8 GPa | ASTM D638 |
Elongation | 23.0 °C | 1.3 % Show Supplier Material materials with Elongation of 1.3 % | ASTM D638 | brk, Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 2.5 GPa Show Supplier Material materials with Flexural modulus of 2.5 GPa | ASTM D 790 | 1.3 mm/min |
Impact strength, Izod notched | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 30 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 30 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 30 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 273 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 273 J/m | ASTM D 256 | un-notched, 23°C |
Tensile strength | 23.0 °C | 34 MPa Show Supplier Material materials with Tensile strength of 34 MPa | ASTM D638 | brk, Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.1E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5.1E-5 1/K | ASTM E 831 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 52 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 52 1/K | ASTM E 831 | ||
Heat deflection temperature | 210 °C Show Supplier Material materials with Heat deflection temperature of 210 °C | ||||
Heat deflection temperature, 1.80 MPa | 210 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 210 °C | ASTM D648 | 3.2 mm, unannealed | |||
Vicat softening temperature | 220 °C Show Supplier Material materials with Vicat softening temperature of 220 °C | ASTM D 1525 | |||
Flammability | UL94 Flame Class Rating: 5VA- UL 94 <br> OSU total heat release (2 minute test): 5kW-min/m² FAR 25.853 <br> FAA Flammability: Passed- FAR 25.853 <br> OSU peak heat release rate (5 minute test): 23kW/m² FAR 25.853 <br> UL94 Flame Class Rating: V0- UL 94 <br> UL94 Flame Class Rating: V0- UL 94 <br> UL94 Flame Class Rating: V0- UL 94 <br> Vertical Burn (60s) passes at: 2sec FAR 25.853 <br> Vertical Burn (12s) passes at: 0sec FAR 25.853 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant | 23.0 °C | 2.9 [-] Show Supplier Material materials with Dielectric constant of 2.9 [-] | ASTM D150 |
Dissipation factor | 23.0 °C | 3E-3 [-] Show Supplier Material materials with Dissipation factor of 3E-3 [-] | ASTM D150 |
Volume resistivity | 23.0 °C | 1.26E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.26E+15 Ω·cm | ASTM D 257 |
Technological properties
Property | ||
---|---|---|
Application areas | Fused Deposition Modeling (FDM), Additive Plastic | |
Availability | Europe,Americas | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |