General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.45 g/cm³ Show Supplier Material materials with Density of 1.45 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.45 [-] Show Supplier Material materials with Relative density of 1.45 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.3 % Show Supplier Material materials with Water absorption of 0.3 % | ASTM D 570 | (23°C/Saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 13.9 GPa Show Supplier Material materials with Elastic modulus of 13.9 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2 % Show Supplier Material materials with Elongation of 2 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 12.3 GPa Show Supplier Material materials with Flexural modulus of 12.3 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 280 MPa Show Supplier Material materials with Flexural strength of 280 MPa | ISO 178 | yield, 2 mm/min |
Hardness, Rockwell R | 23.0 °C | 108 [-] Show Supplier Material materials with Hardness, Rockwell R of 108 [-] | ASTM D 785 |
Impact strength, Charpy notched | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179/2C | -30°C |
Impact strength, Izod notched | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 90 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 90 J/m | ASTM D 256 |
Tensile strength | 23.0 °C | 198 MPa Show Supplier Material materials with Tensile strength of 198 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.6E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature | 244 - 258 °C Show Supplier Material materials with Heat deflection temperature of 244 - 258 °C | ||
Heat deflection temperature, 0.45 MPa | 258 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 258 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 244 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 244 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Vicat softening temperature | 246 °C Show Supplier Material materials with Vicat softening temperature of 246 °C | ISO 306 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 10 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 10 cm³/10min | ISO 1133 | MVR at 220°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.24 % Show Supplier Material materials with Shrinkage of 0.24 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.6 % Show Supplier Material materials with Shrinkage, transverse of 0.6 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | EV Infrastructure, Electronic Components, Transmission/Transfer Comp, Personal Computing | |
Availability | Europe,Asia,Americas | |
Processing methods | Minimum Moisture Content: 0.02% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |