General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.107 g/cm³ Show Supplier Material materials with Density of 1.107 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 1 % Show Supplier Material materials with Moisture absorption of 1 % | ASTM D 570 | (50% RH, Equilibrium) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 60 % Show Supplier Material materials with Elongation of 60 % | ASTM D 638 | brk, Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.2 GPa Show Supplier Material materials with Flexural modulus of 2.2 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Flexural strength | 23.0 °C | 95 MPa Show Supplier Material materials with Flexural strength of 95 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Impact strength, Izod notched | 23.0 °C | 240 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 240 kJ/m² | ASTM D 256 | notched, 23°C |
Tensile strength | 23.0 °C | 59 MPa Show Supplier Material materials with Tensile strength of 59 MPa | ASTM D 638 | yld, Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.26E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.26E-4 1/K | ASTM E 831 | 60°C to 138°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 1.26E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.26E-4 1/K | ASTM E 831 | 60°C to 138°C |
Heat deflection temperature | 193 °C Show Supplier Material materials with Heat deflection temperature of 193 °C | ||
Heat deflection temperature, 0.45 MPa | 193 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 193 °C | ASTM D 648 | 6.4 mm, unannealed | |
Vicat softening temperature | 232 °C Show Supplier Material materials with Vicat softening temperature of 232 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 1.1 % Show Supplier Material materials with Shrinkage of 1.1 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Heavy Vehicles, Head Protection, Energy Absorber, Door Handle, Document Handling, Console, Cladding, Auto Aftermarket, Pump, Small Appliance, Medical Device, Wheel Cover | |
Availability | Europe,Asia,Americas | |
Processing methods | Rear - Zone 1 Temperature: 265 to 305.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |