NORYL GTX™ Resin GTX910 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ 910 resin is non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). NORYL GTX910 resin exhibits excellent chemical resistance and is an excellent candidate for automotive applications such as plastic/metal hybrid components, rail extensions, crash cans, wheel covers, and energy absorbers.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Healthcare

Medical Equipment

Ophthalmics

Electronics

Display Devices

Automotive

General Automotive Parts

Crash & Chassis

Automotive Exterior

Automotive Interior

Construction

Water Management

Consumer Goods

Domestic Electrical Appliances

Show all

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.107 g/cm³ Show Supplier Material materials with Density of 1.107 g/cm³	ASTM D 792
Moisture absorption	23.0 °C	0.5 % Show Supplier Material materials with Moisture absorption of 0.5 %	ASTM D 570 \| (23°C/50% RH/24 hrs)

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	60 % Show Supplier Material materials with Elongation of 60 %	ASTM D 638 \| brk, Type I, 50 mm/min
Flexural modulus	23.0 °C	2.2 GPa Show Supplier Material materials with Flexural modulus of 2.2 GPa	ASTM D 790 \| 2.6 mm/min, 100 mm span
Flexural strength	23.0 °C	95 MPa Show Supplier Material materials with Flexural strength of 95 MPa	ASTM D 790 \| yld, 2.6 mm/min, 100 mm span
Impact strength, Izod notched	23.0 °C	240 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 240 kJ/m²	ASTM D 256 \| notched, 23°C
Tensile strength	23.0 °C	59 MPa Show Supplier Material materials with Tensile strength of 59 MPa	ASTM D 638 \| yld, Type I, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 9E-5 1/K	ASTM E 831 \| -40°C to 95°C
Coefficient of thermal expansion, transverse	23.0 °C	1.26E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.26E-4 1/K	ASTM E 831 \| 60°C to 138°C
Heat deflection temperature		193 °C Show Supplier Material materials with Heat deflection temperature of 193 °C
Heat deflection temperature, 0.45 MPa		193 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 193 °C	ASTM D 648 \| 6.4 mm, unannealed
Vicat softening temperature		232 °C Show Supplier Material materials with Vicat softening temperature of 232 °C	ASTM D 1525 \| Rate B/50

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	1.2 % Show Supplier Material materials with Shrinkage of 1.2 %	SABIC method \| on tensile bar

Technological properties

Property
Application areas	Heavy Vehicles, Head Protection, Energy Absorber, Door Handle, Document Handling, Console, Cladding, Auto Aftermarket, Pump, Small Appliance, Medical Device, Wheel Cover
Availability	Europe,Asia,Americas
Processing methods	Screw Speed: 20 to 100.0rpm Rear - Zone 1 Temperature: 265 to 305.0°C Drying Time: 3 to 4.0hrs Drying Temperature: 95 to 105.0°C Front - Zone 3 Temperature: 275 to 305.0°C Middle - Zone 2 Temperature: 270 to 305.0°C Melt Temperature: 280 to 305.0°C Mold Temperature: 75 to 120.0°C Shot to Cylinder Size: 30 to 50.0% Maximum Moisture Content: 0.07% Back Pressure: 0.3 to 1.4MPa Drying Time (Cumulative): 8hrs Minimum Moisture Content: 0.02% Nozzle Temperature: 280 to 305.0°C Vent Depth: 0.013 to 0.038mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.